Microporous products

ABSTRACT

Novel microporous polymers in forms ranging from films to blocks and intricate shapes from synthetic thermoplastic polymers, such as, olefinic, condensation, and oxidation polymers, are disclosed. In one embodiment the microporous polymers are characterized by a relatively homogeneous, three-dimensional cellular structure having cells connected by pores of smaller dimension. Also disclosed are microporous polymer products which contain relatively large amounts of functionally useful liquids and behave as solids.

This is a continuation of application Ser. No. 814,351, filed 07-11-77;which is a continuation-in-part of Ser. No. 718,549, filed 08-30-76,both abandoned.

RELATED APPLICATIONS

Castro and Stoll, Ser. No. 622,643, filed: Oct. 15, 1975, for: SolidAntistat Compositions; a continuation-in-part of Ser. No. 436,252,filed: Jan. 24, 1974, now abandoned.

BACKGROUND OF THE INVENTION

This invention relates to porous polymer structures and a method ofpreparing the same. More particularly, this invention relates tomicroporous polymer structures that may be readily prepared and arecharacterized by relatively homogeneous, three-dimensional, cellularmicrostructures and to a unique, facile process for preparingmicroporous polymer structures.

Several widely differing techniques have been previously developed forpreparing microporous polymer structures. Such techniques range fromwhat is termed, in the art, classical phase inversion, to nuclearbombardment, to incorporation of microporous solid particles in asubstrate which are subsequently leached out, to sintering microporousparticles together in some fashion. Prior efforts in the field haveentailed still other techniques as well as innummerable variations ofwhat may be considered as the classical or basic techniques.

The interest in microporous polymer products has been engendered by thenumerous potential applications for materials of this type. Thesepotential applications are well known and range from ink pads, or thelike, to leather-like breathable sheets, to filter media. Yet, with allof the potential applications, the commercial usage has been relativelymodest. And, the techniques being commercially utilized have variouslimitations which do not allow the versatility required to expand theapplications to reach the potential market for microporous products.

As mentioned, some commercially available microporous polymer productsare made by a nuclear bombardment technique. Such a technique is capableof achieving a rather narrow pore size distribution; however, the porevolume must be relatively low (i.e.--less than about 10% void space) toensure that the polymer will not be degraded during preparation. Manypolymers cannot be utilized in such a technique due to the lack of theability of the polymer to etch. Still further, the technique requiresthat a relatively thin sheet or film of the polymer be used andconsiderable expertise must be employed in carrying out the procedure toavoid "double tracking", which results in the formation of oversizedpores.

Classical phase inversion has also been commercially utilized to formmicroporous polymers from cellulose acetate and certain other polymers.Classical phase inversion has been reviewed in great detail by R. E.Kesting in SYNTHETIC POLYMERIC MEMBRANES, McGraw-Hill, 1971. Inparticular at page 117 of said reference it is explicitly stated thatclassical phase inversion involves the use of at least three components,a polymer, a solvent for said polymer and a non-solvent for saidpolymer.

Reference may also be made to U.S. Pat. No. 3,945,926 which teaches theformation of polycarbonate resin membranes from a casting solutioncontaining the resin, a solvent, and a swelling agent and/or anonsolvent. It is stated at lines 42-47, column 15, of said patent thatin the complete absence of a swelling agent phase inversion usually doesnot occur and that with low concentrations of swelling agents,structures possessing closed cells are encountered.

From the foregoing discussion it is quite apparent that classical phaseinversion requires the use of a solvent for the system at roomtemperature so that many other useful polymers cannot be substituted forthe polymers such as cellulose acetate. Also from the processstandpoint, the classical phase inversion process will generally berestricted to the formation of films due to the large amount of solventused in the preparation of solutions which must be subsequentlyextracted. It is also apparent that classical phase inversion requires arelatively high degree of process control to obtain structures ofdesired configuration. Thus the relative concentrations of solvent,nonsolvent, and swelling agent must be critically controlled, asdiscussed in column 14-16 of U.S. Pat. No. 3,945,926. Conversely, toalter the number, size, and homogeneity of the resultant structure, onemust modify the aforementioned parameters by trial-and-error.

Other commercially available microporous polymers are made by sinteringmicroporous particles of polymers ranging from high density polyethyleneto polyvinylidene fluoride. However, it is difficult with such atechnique to obtain a product with the narrow pore size distributionrequired for many applications.

A still further general technique which has been the subject ofconsiderable prior effort involves heating a polymer with variousliquids to form a dispersion or solution and thereafter cooling,followed by removal of the liquid with a solvent or the like. This typeof process is disclosed in the following United States patents which areonly representative and not cumulative U.S. Pat. Nos.: 3,607,793;3,378,507; 3,310,505; 3,748,287; 3,536,796; 3,308,073; and 3,812,224. Itis not believed that the foregoing technique has been utilizedcommercially to any significant extent, if at all, probably due to thelack of economic feasibility of the particular processes which havepreviously been developed. Also, the prior processes do not allow thepreparation of microporous polymers which combine relatively homogeneousmicrocellular structures with the pore size and pore size distributionswhich are typically desired.

With respect to the microporous polymers obtained by prior arttechniques, no process known heretofore has been capable of yieldingisotropic olefinic or oxidation polymers which have the major portion ofpore sizes in the range of about 0.1 to about 5 microns while having arelatively narrow pore size ditribution, thus exhibiting a high degreeof pore size uniformity throughout a sample thereof. Some prior artolefinic or oxidation polymers have had pore sizes in the foregoingrange, but without a relatively narrow pore size distribution, thusmaking such materials without significant value in application areas,such as filtration, which require a high degree of selectivity.Furthermore, prior microporous olefinic or oxidation polymers which maybe considered to have relatively narrow pore size distributions have hadabsolute pore sizes which are outside the aforementioned range, usuallyhaving substantially smaller pore sizes, for use in application areassuch as ultra-filtration. Finally, some prior art olefinic polymers havehad pore sizes in the foregoing range and what may be considered to berelatively narrow pore size distributions. However, such materials havebeen made by use of techniques, such as stretching which impart a highdegree of orientation to the resultant anisotropic material, renderingit undesirable for many application areas. There thus has existed a needfor microporous olefinic and oxidation polymers having a pore size in arange of from about 0.1 to about 5 microns and characterized as having arelatively narrow isotropic pore size distribution.

Also, a major drawback of many microporous polymers available heretoforehas been the low flow rate of such polymers when used in structures suchas microfiltration membranes. One of the major reasons for such low flowrates is the typically low void volume of many such polymers. Thus,perhaps 20 percent of the polymer structure, or less, may be "void"volume through which a filtrate may flow, the remaining 80 percent ofthe structure being the polymer resin which forms the microporousstructure. Thus, there has also existed a need for microporous polymershaving a high degree of void volume, especially with respect to olefinicpolymers.

The copending Castro and Stoll application, previously identifiedherein, discloses a highly advantageous method for converting aparticular type of liquid amine antistatic agent to a material whichbehaves as a solid. The advantages in processing which result are realand significant. It would be similarly beneficial to be able to convertother useful functional liquids such as flame retardants and the like tomaterials which behave as solids.

It is accordingly an object of the present invention to providemicroporous polymer products characterized by relative homogeneity andnarrow pore size distributions.

Another object is to provide a facile process which allows the economicproduction of microporous polymers.

A still further object lies in the provision of a process for makingmicroporous polymer products, which has applicability to a wide numberof useful thermoplastic polymers. A related and more specific object isto provide such a process which is capable of readily formingmicroporous polymers from any synthetic thermoplastic polymer includingpolyolefins, condensation polymers and oxidation polymers.

Yet another object of this invention is to provide microporous polymersin structures ranging from thin films to relatively thick blocks. Arelated object is to provide the ability to form microporous polymers inintricate shapes.

A further object is to provide the conversion of functional liquids tomaterials which possess the characteristics of a solid.

Other objects and advantages of the present invention will becomeapparent from the following discussion, and from the drawings, in which:

FIG. 1 is a graph of temperature vs. concentration for a hypotheticalpolymer-liquid system, setting forth the binodial and spinodal curves,and illustrating the concentration necessary to achieve the microporouspolymers and to practice the process of the present invention;

FIG. 1A is a graph of temperature vs. concentration similar to that ofFIG. 1, but also including the freezing point depression phase line;

FIG. 2 is a photomicrograph, at 55X amplification, showing themacrostructure of a polypropylene microporous polymer of the presentinvention with about a 75 percent void volume;

FIGS. 3 through 5 are photomicrographs of the microporous polypropylenestructure of FIG. 2 at, respectively, 550X, 2200X and 5500Xamplification, and illustrate a homogeneous cellular structure;

FIGS. 6 through 10 are photomicrographs at, respectively, 1325X, 1550X,1620X, 1450X and 1250X amplification of additional microporouspolypropylene structures and show the modifications in the structure asthe void space is reduced from 90%, to 70%, to 60%, to 40%, and to 20%,respectively;

FIGS. 11 through 13 are photomicrographs at, respectively, 2000X, 2050Xand 1950X amplification of still further microporous polypropylenestructures of the present invention and illustrate the decreasing cellsize as the polypropylene content is increased from the 10% by weightlevel in FIG. 11, to 20%, and to 30%, in FIGS. 12 and 13, respectively;

FIGS. 14 through 17 are photomicrographs at, respectively, 250X, 2500X,2500X and 2475X amplification of microporous low density polyethylenestructures of the present invention, FIGS. 14 and 15 showing the macro-and microstructure of a microporous polymer containing 20% by weightpolyethylene and FIGS. 16 and 17 showing the microstructure with 40% and70% polyethylene respectively;

FIGS. 18 and 19 are photomicrographs at, respectively, 2100X and 2000Xamplification of microporous high density polyethylene structures of thepresent invention and illustrate the structures at 30% and 70% by weightpolyethylene, respectively;

FIGS. 20 and 21 are photomicrographs, at, respectively, 2550X and 2575Xamplification of microporous SBR polymers of the present invention andshow a homogeneous cellular structure;

FIG. 22 is a photomicrograph at 2400X amplification of a microporousmethylpentene polymer;

FIGS. 23 and 24 are photomicrographs at, respectively, 255X and 2550Xamplification of a microporous ethylene-acrylic acid copolymer;

FIG. 25 is a photomicrograph at 2500X amplification of a microporouspolymer formed from a polyphenylene oxide-polystyrene blend;

FIG. 26 is a photomicrograph at 2050X amplification and illustrates apolystyrene microporous polymer;

FIG. 27 is a photomicrograph at 2000X amplification and showing apolyvinylchloride microporous polymer;

FIGS. 28 and 29 are photomicrographs at 2000X amplification of lowdensity polyethylene microporous polymers and showing the partialmasking of the basic structure by the "foliage" mode structure;

FIGS. 30 and 33 are mercury intrusion curves of microporouspolypropylene structures of the present invention and illustrating thenarrow pore diameter distribution which is characteristic of thepolymers of the instant invention;

FIGS. 34 to 40 are mercury intrusion curves of commercial microporousproducts including "Celgard" polypropylene (FIG. 34), "Amerace A20" and"Amerace A30" polyvinyl chloride (FIGS. 35 and 36 respectively), "Porex"polypropylene (FIG. 37), "Millipore BDWP 29300" cellulose acetate (FIG.38), "Gelman TCM-200" cellulose triacetate and "Gelman Acropor WA"acrylonitrile-polyvinyl chloride copolymer (FIGS. 39 and 40respectively);

FIGS. 41 through 43 are mercury intrusion curves of microporousstructures made in accordance with U.S. Pat. No. 3,378,507, usingpolyethylene (FIGS. 41 and 42) and polypropylene (FIG. 43);

FIG. 44 is a mercury intrusion curve of a polyethylene microporousmaterial made in accordance with U.S. Pat. No. 3,310,505;

FIGS. 45 to 46 are photomicrographs of a porous polyethylene productprepared by duplicating Example 2 of U.S. Pat. No. 3,378,507 using aninjection molding technique, FIG. 45 (240X amplification) showing themacrostructure and FIG. 46 (2400X amplification) showing themicrostructure;

FIGS. 47 to 48 are photomicrographs of a porous polyethylene productprepared by duplicating Example 2 of U.S. Pat. No. 3,378,507 using acompression molding technique, FIG. 47 (195X amplification) showing themacrostructure and FIG. 48 (2000x amplification) showing themicrostructure;

FIGS. 49 to 50 are photomicrographs of a porous polypropylene productprepared by duplicating Example 2 of U.S. Pat. No. 3,378,507 using aninjection molding technique, FIG. 49 (195X amplification) showing themacrostructure and FIG. 50 (2000X amplification) showing themicrostructure;

FIGS. 51 to 52 are photomicrographs of a porous polypropylene productprepared by duplicating Example 2 of U.S. Pat. No. 3,378,507 using acompression molding technique, FIG. 51 (206X amplification) showing themacrostructure and FIG. 52 (2000X amplification) showing themicrostructure, and

FIGS. 53 to 54 are photomicrographs of a porous polyethylene productprepared by duplicating Example 2 of U.S. Pat. No. 3,310,505, FIG. 53(205 amplification) showing the macrostructure and FIG. 54 (200Xamplification) showing the microstructure.

FIG. 55 shows a melt curve and a crystallization curve for apolypropylene and quinoline polymer/liquid system.

FIG. 56 shows a melt curve and several crystallization curves for apolypropylene and N,N bis(2-hydroxyethyl)tallow-amine polymer/liquidsystem.

FIG. 57 shows a melt curve and a crystallization curve for apolypropylene and dioctyl phthalate polymer/liquid system, demonstratinga system which is not within the scope of the present invention.

FIG. 58 shows the phase diagram for a low molecular weight polyethyleneand diphenyl ether polymer/liquid system, determined at cooling andheating rates of 1° C./minute.

FIG. 59 shows several melt and crystallization curves for a lowmolecular weight polyethylene and diphenyl ether polymer/liquid system.

FIG. 60 shows a glass transition curve for a low molecular weightpolystyrene and 1-dodecanol polymer/liquid system.

FIG. 61 is a photomicrograph at 5000X amplification of a 70 percent voidmicroporous cellular structure of the present invention, made frompolymethylmethacrylate.

FIG. 62 shows melt and crystallization curves for a Nylon 11 andtetramethylene sulfone polymer/liquid system.

FIG. 63 is a photomicrograph at 2000X amplification of a 70 percent voidmicroporous cellular structure of the present invention, made from Nylon11.

FIG. 64 is a photomicrograph at 2000X amplification of a 70 percent voidmicroporous cellular structure of the present invention, made frompolycarbonate.

FIG. 65 is a photomicrograph at 2000X amplification of a 70 percent voidmicroporous cellular structure of the present invention, made frompolyphenylene oxide.

FIGS. 66 and 67 are photomicrographs at 2000X amplification of a 60percent void and a 75 percent void, respectively, microporousnon-cellular structure of the present invention, made frompolypropylene.

FIGS. 68 and 69 are, respectively, mercury intrusion curves of a 60percent void and a 75 percent void non-cellular microporouspolypropylene structure within the scope of the present invention.

FIG. 70 is a graphical representation of the unique microporous cellularstructures of the present invention as compared to certain prior artcompositions.

While the invention is susceptible of various modifications andalternative forms, there will be herein described in detail thepreferred embodiments. It is to be understood, however, that it is notintended to limit the invention to the specific forms disclosed. On thecontrary, it is intended to cover all modifications and alternativeforms falling within the spirit and scope of the invention as expressedin the appended claims.

SUMMARY OF THE INVENTION

It has now been discovered that any synthetic thermoplastic polymer maybe rendered microporous by first heating said polymer and a compatibleliquid, discussed hereinbelow, to a temperature and for a timesufficient to form a homogeneous solution. The so formed solution isthen allowed to assume a desired shape and subsequently cooled in saidshape at a rate and to a temperature sufficient so that thermodynamicnon-equilibrium liquid-liquid phase separation is initiated. As thesolution is cooled in the desired shape, no mixing or other shear forceis applied while the solution is undergoing the cooling. The cooling iscontinued so that a solid results. The solid needs only to attainsufficient mechanical integrity to allow it to be handled, withoutcausing physical degradation. Finally, at least a substantial portion ofthe compatible liquid is removed from the resulting solid to form thedesired microporous polymer.

Certain novel microporous olefinic and oxidation polymers of the presentinvention are characterized by a narrow pore size distribution, asdetermined by mercury intrusion porosimetry. The narrow pore sizedistribution may be analytically expressed in terms of a sharpnessfunction "S" which is explained in detail hereinbelow. The "S" values ofthe olefinic and oxidation polymer of the present invention range fromabout 1 to about 10. Also, said polymers of the present invention arecharacterized by average pore sizes which range from about 0.10 to about5 microns about 0.2 to about 1 micron being preferred. Furthermore, suchmicroporous products are substantially isotropic, and thus haveessentially the same cross-sectional configuration when analyzed alongany spatial plane.

In another aspect of the present invention the method of preparingmicroporous polymers is performed so that a mixture comprising asynthetic thermoplastic polymer, especially a polyolefin, anethylene-acrylic acid copolymer, a polyphenylene oxide-polystyreneblend, or a blend of one or more of the foregoing polymers, and acompatible liquid is heated to a temperature and for a time sufficientto form a homogeneous solution. The solution is then cooled, thusforming at substantially the same time a plurality of liquid droplets ofsubstantially the same size. The cooling is then continued to solidifythe polymer and at least a substantial portion of the liquid is removedfrom the resulting solid to form the desired cellular polymer structure.

The foregoing method will result in microporous polymer productscharacterized by a cellular, three-dimensional, void microstructure,i.e.--a series of enclosed cells having substantially spherical shapesand pores or passageways interconnecting adjacent cells. The basicstructure is relatively homogeneous with the cells being uniformlyspaced throughout the three dimensions, and the interconnecting poreshave diameters which are relatively narrow in size distribution asmeasured by mercury intrusion. For ease of reference, microporouspolymers having such a structure will be referred to as "cellular."

A related aspect of this invention provides novel microporous polymerproducts which behave as solids and contain relatively large amounts offunctionally useful liquids such as, for example, polymer additivesincluding flame retardants and the like. In this fashion, useful liquidsmay obtain the processing advantages of a solid material which may beused directly, as for example, in a master batch. Such products may beformed directly by using a functional liquid as the compatible liquidand not carrying out the removal of the compatible liquid or indirectlyby either reloading the microporous polymer after the removal of thecompatible liquid or displacing the compatible liquid before removal toincorporate the functional liquid.

DETAILED DESCRIPTION OF THE INVENTION

Broadly, the practice of the process of the instant invention involvesheating the desired polymer with an appropriate compatible liquid toform a homogeneous solution, cooling said solution in an appropriatemanner to form a solid material and subsequently extracting the liquidto form a microporous material. The considerations involved inpracticing the instant invention will be described in detailhereinbelow.

SELECTION OF THE POLYMER

As indicated, the present invention surprisingly affords a technique forrendering any synthetic thermoplastic polymer microporous. Thus, theprocess of the present invention applies to olefinic polymers,condensation polymers, and oxidation polymers.

Exemplary of the useful non-acrylic polyolefins are low densitypolyethylene, high density polyethylene, polypropylene, polystyrene,polyvinylchloride, acrylonitrile-butadiene-styrene terpolymers,styrene-acrylonitrile copolymers, styrene butadiene copolymers,poly(4-methyl-pentene-1), polybutylene, polyvinylidene chloride,polyvinyl butyral, chlorinated polyethylene, ethylene-vinyl acetatecopolymers, polyvinyl acetate, and polyvinyl alcohol.

Useful acrylic polyolefins include polymethyl-methacrylate,polymethyl-acrylate, ethylene-acrylic acid copolymers, andethylene-acrylic acid metal salt copolymers.

Polyphenylene oxide is representative of the oxidation polymers whichmay be utilized. The useful condensation polymers include polyethyleneterephthalate, polybutylene terephthalate, Nylon 6, Nylon 11, Nylon 13,Nylon 66, polycarbonates and polysulfone.

SELECTION OF THE COMPATIBLE LIQUID

Thus, to practice the present invention one need only first choose thesynthetic thermoplastic polymer which is to be rendered microporous.Having selected the polymer, the next procedure is the selection of theappropriate compatible liquid and the relative amounts of polymer andliquid to be utilized. Of course blends of one or more polymers may beutilized in the practice of the present invention. Functionally, thepolymer and liquid are heated with stirring up to the temperaturerequired to form a clear, homogeneous solution. If a solution cannot beformed at any liquid concentration, then the liquid is inappropriate andcannot be utilized with that particular polymer.

Because of the selectivity, absolute predictability for predeterminingthe operability of a particular liquid with a particular polymer is notpossible. However, some useful general guidelines can be set forth. Thuswhen the polymer involved is non-polar, non-polar liquids with similarsolubility parameters at the solution temperature are more likely to beuseful. When such parameters are not available, one may refer to themore readily available room temperature solubility parameters, forgeneral guidance. Similarly, with polar polymers, polar organic liquidswith similar solubility parameters should be initially examined. Also,the relative polarity or non-polarity of the liquid should be matchedwith the relative polarity or non-polarity of the polymer. In addition,with hydrophobic polymers, useful liquids will typically have little orno water solubility. On the other hand, polymers which tend to behydrophilic will generally require a liquid having some watersolubility.

With respect to appropriate liquids, particular species of various typesof organic compounds have been found useful, including aliphatic andaromatic acids, aliphatic, aromatic and cyclic alcohols, aldehydes,primary and secondary amines, aromatic and ethoxylated amines, diamines,amides, esters and diesters, ethers, ketones and various hydrocarbonsand heterocycles. It should, however, be noted tha the concept is quiteselective. Thus, for example, not all saturated aliphatic acids will beuseful; and, further, not all liquids useful for high densitypolyethylene will necessarily be useful for, as an example, polystyrene.

As will be appreciated, the useful proportions of polymer and liquid forany particular system can readily be developed from an evaluation of theparameters which will be discussed subsequently.

Where blends of one or more polymers are used, as should be understood,useful liquids must typically be operable with all of the polymersincluded. It may however be possible for the polymer blend to havecharacteristics such that the liquid need not be operable with allpolymers used. As one example, where one or more polymeric constituentsare present in such relatively small amounts as to not significantlyaffect the properties of the blend, the liquid employed need only beoperable with the principal polymer or polymers.

Also, while most useful materials are liquids at ambient temperatures,materials which are solid at room temperature may be employed so long assolutions can be formed with the polymer at elevated temperatures andthe material does not interfere with the formation of the microporousstructure. More specifically, a solid material may be used so long asphase separation occurs by liquid-liquid separation rather thanliquid-solid separation during the cooling step which will hereinafterbe discussed. The amount of liquid used can be, in general, varied fromabout 10 to about 90%.

As presently discussed any synthetic thermoplastic polymer may beemployed so long as the liquid selected forms a solution with thepolymer and the concentration yields a continuous polymer phase uponseparation during cooling, as will be discussed in more detailhereinafter. So that one may appreciate the range of operable polymerand liquid systems, a brief summary of some of such systems may beuseful.

In forming microporous polymers from polypropylene, alcohols such as2-benzylamino-2-propanol and 3-phenyl-1-propanol; aldehydes such assalicylaldehyde; amides such as N,N-diethyl-m-toluamide; amines such asN-hexyl diethanolamine, N-behenyl diethanol amine,N-coco-diethanolamine, benzyl amine, N,N-bis-β-hydroxyethyl cyclohexylamine, diphenyl amine and 1,12-diamino dodecane; esters such as methylbenzoate, benzyl benzoate, phenyl salicylate, methyl salicylate anddibutyl phthalate; and ethers such as diphenyl ether, 4-bromodiphenylether and dibenzyl ether have been found useful. In addition,halocarbons such as 1,1,2,2-tetrabromoethane and hydrocarbons such astrans-stilbene and other alkyl/aryl phosphites are also useful as areketones such as methyl nonyl ketone.

In forming microporous polymers from high density polyethylene, asaturated aliphatic acid such as decanoic acid, primary saturatedalcohols such as decyl alcohol, and 1-dodecanol, secondary alcohols suchas 2-undecanol and 6-undecanol, ethoxylated amines such asN-lauryldiethanolamine, aromatic amines such as N,N-diethylaniline,diesters such as dibutyl sebacate and dihexyl sebacate and ethers suchas diphenyl ether and benzyl ether have been found useful. Other usefulliquids include halogenated compounds such as octabromodiphenyl,hexabromobenzene and hexabromocyclodecane, hydrocarbons such as1-hexadecane, diphenylmethane and naphthalene, aromatic compounds suchas acetophenone and other organic compounds such as alkyl/arylphosphites, and quinoline and ketones such as methylnonyl ketone.

To form microporous polymers from low density polyethylene, thefollowing liquids have been found useful: saturated aliphatic acidsincluding hexanoic acid, caprylic acid, decanoic acid, undecanoic acid,lauric acid, myristic acid, palmitic acid and stearic acid, unsaturatedaliphatic acids including oleic acid and erucic acid, aromatic acidsincluding benzoic acid, phenyl stearic acid, polystearic acid and xylylbehenic acid and other acids including branched carboxylic acids ofaverage chain lengths of 6, 9, and 11 carbons, tall oil acids and rosinacid, primary saturated alcohols including 1-octanol, nonyl alcohol,decyl alcohol, 1-decanol, 1-dodecanol, tridecyl alcohol, cetyl alcoholand 1-heptadecanol, primary unsaturated alcohols including undecylenylalcohol and oleyl alcohol, secondary alcohols including 2-octanol,2-undecanol, dinonyl carbinol and diundecyl carbinol and aromaticalcohols including 1-phenyl ethanol, 1-phenyl-1-pentanol, nonyl phenol,phenylstearyl alcohol and 1-naphthol. Other useful hydroxyl-containingcompounds include polyoxyethylene ethers of oleyl alcohol and apolypropylene glycol having a number average molecular weight of about400. Still further useful liquids include cyclic alcohols such as4,t-butyl cyclohexanol and menthol, aldehydes including salicylaldehyde, primary amines such as octylamine, tetradecylamine andhexadecylamine, secondary amines such as bis-(1-ethyl-3-methylpentyl)amine and ethoxylated amines including N-lauryl diethanolamine,N-tallow diethanol-amine, N-stearyl diethanolamine and N-cocodiethanolamine.

Additional useful liquids comprise aromatic amines includingN-sec-butylaniline, dodecylaniline, N,N-dimethylaniline,N,N-diethylaniline, p-toluidine, N-ethyl-o-toluidine, diphenylamine andaminodiphenylmethane, diamines including N-erucyl-1,3-propane diamineand 1,8-diamino-p-menthane, other amines including branched tetraminesand cyclododecylamine, amides including cocoamide, hydrogenated tallowamide, octadecylamide, eruciamide, N,N-diethyl toluamide andN-trimethylolpropane stearamide, saturated aliphatic esters includingmethyl caprylate, ethyl laurate, isopropyl myristate, ethyl palmitate,isopropropyl palmitate, methyl stearate, isobutyl stearate and tridecylstearate, unsaturated esters including stearyl acrylate, butylundecylenate and butyl oleate, alkoxy esters including butoxyethylstearate and butoxyethyl oleate, aromatic esters including vinyl phenylstearate, isobutyl phenyl stearate, tridecyl phenyl stearate, methylbenzoate, ethyl benzoate, butyl benzoate, benzyl benzoate, phenyllaurate, phenyl salicylate, methyl salicylate and benzyl acetate anddiesters including dimethyl phenylene distearate, diethyl phthalate,dibutyl phthalate, di-iso-octyl phthalate, dicapryl, adipate, dibutylsebacate, dihexyl sebacate, di-isooctyl sebacate, dicapryl sebacate anddioctyl maleate. Yet other useful liquids comprise polyethylene glycolesters including polyethylene glycol (having an average molecular weightof about 400), diphenylstearate, polyhydroxylic esters including castoroil (triglyceride), glycerol monostearate, glycerol monooleate, glyceroldistearate glycerol dioleate and trimethylol propane monophenylstearate,ethers including diphenyl ether and benzyl ether, halogenated compoundsincluding hexachlorocyclopentadiene, octabromobiphenyl,decabromodiphenyl oxide and 4-bromodiphenyl ether, hydrocarbonsincluding 1-nonene, 2-nonene, 2-undecene, 2-heptadecene, 2-nonadecene,3-eicosene, 9-nonadecene, diphenylmethane, triphenylmethane andtrans-stilbene, aliphatic ketones including 2-heptanone, methyl nonylketone, 6-undecanone, methylundecyl ketone, 6-tridecanone,8-pentadecanone, 11-pentadecanone, 2-heptadecanone, 8-heptadecanone,methyl heptadecyl ketone, dinonyl ketone and distearyl ketone, aromaticketones including acetophenone and benzophenone and other ketonesincluding xanthone. Still further useful liquids comprise phosphorouscompounds including trixylenyl phosphate, polysiloxanes, Muget hyacinth(An Merigenaebler, Inc), Terpineol Prime No. 1 (Givaudan-Delawanna,Inc), Bath Oil Fragrance #5864 K (International Flavor & Fragrance, Inc)Phosclere P315C (organophosphite), Phosclere P576 (organophosphite),styrenated nonyl phenol, quinoline and quinalidine.

To form microporous polymer products with polystyrene, useful liquidsinclude tris-halogenated propylphosphate, aryl/alkyl phosphites, 1,1,2,2tetrabromoethane, tribromoneopentylalcohol, 40% Voranol C.P. 3000 polyoland tribromoneopentyl alcohol 60%, tris-β-chloroethylphosphate,tris(1,3-dichloroisopropyl)phosphate, tri-(dichloropropyl)phosphate,dichlorobenzene, and 1-dodecanol.

In forming microporous polymers using polyvinyl chloride, useful liquidscomprise aromatic alcohols including methoxy benzyl alcohol,2-benzylamino-1-propanol, and other hydroxyl-containing liquidsincluding 1,3-dichloro-2-propanol. Still other useful liquids comprisehalogenated compounds including Firemaster T33P (tetrabromophthalicdiester), and aromatic hydrocarbons including trans-stilbene.

In addition, in accordance with the present invention, microporousproducts have been made from other polymers and copolymers and blends.Thus, to form microporous products from styrene-butadiene copolymers,useful liquids include decyl alcohol, N-tallow diethanol amine, N-cocodiethanol amine and diphenyl amine. Useful liquids for formingmicroporous polymers from ethylene-acrylic acid copolymer salts includeN-tallow diethanolamine, N-coco diethanolamine, dibutyl phthalate anddiphenyl ether. Microporous polymer products using high impactpolystyrene can be formed by employing as liquids, hexabromobiphenyl andalkyl/aryl phosphites. With "Noryl" polyphenylene oxide-polystyreneblends (General Electric Company), microporous polymers can be madeutilizing N-coco diethanol amine, N-tallow diethanolamine,diphenylamine, dibutyl phthalate and hexabromophenol. Microporouspolymers from blends of low density polyethylene and chlorinatedpolyethylene can be made by utilizing 1-dodecanol, diphenyl ether andN-tallow diethanolamine. Utilizing 1-dodecanol as the liquid,microporous polymer products can be made from the following blends:polypropylene-chlorinated polyethylene, high densitypolyethylene-chlorinated polyethylene, high densitypolyethylene-polyvinyl chloride and high density polyethylene andacrylonitrile-butadiene-styrene (ABS) terpolymers. To form microporousproducts from polymethylmethacrylate, 1-4,butanediol and lauric acidhave been found to be useful. Microporous Nylon 11 may be made utilizingethylene carbonate, 1,2-propylene carbonate, or tetramethylene sulfone.Also, menthol may be utilized to form microporous products frompolycarbonate.

SELECTION OF THE CONCENTRATIONS OF POLYMER AND LIQUID

The determination of the amount of the liquid used is obtained byreference to the binodial and spinodal curves for the system,illustrative curves being set forth in FIG. 1. As shown therein, T_(m)represents the maximum temperature of the binodial curve (i.e.--themaximum temperature of the system at which binodial decomposition willtake place), T_(ucs) represents the upper critical solution temperature(i.e.--the maximum temperature at which spinodal decomposition will takeplace), φ_(m) represents the polymer concentration at T_(m), φ_(c)denotes the critical concentration and φ_(x) represents the polymerconcentration of the system needed to obtain the unique microporouspolymer structures of the present invention. Theoretically, φ_(m) andφ_(c) should be virtually identical; however, as is known, due tomolecular weight distributions of commercially available polymers, φ_(c)may be about 5% by weight or so greater than the value of φ_(m). To formthe unique microporous polymers of the present invention, the polymerconcentration utilized for a particular system φ_(x), must be greaterthan φ _(c). If the polymer concentration is less than φ_(c), the phaseseparation which will occur as the system is cooled will constitute acontinuous liquid phase with a discontinuous polymer phase. On the otherhand, utilizing the proper polymer concentration will ensure that thecontinuous phase, which will be formed upon cooling to the phaseseparation temperature, will be the polymer phase, as is required toobtain the unique microcellular structures of the present invention.Likewise, as will be apparent, the formation of a continuous polymerphase upon phase separation requires that a solution be initiallyformed. When the process of the present invention is not followed and adispersion is initially formed, the resulting microporous product issimilar to that achieved by sintering together polymer particles.

Accordingly, as will be appreciated, the applicable polymerconcentration or amount of liquid which may be utilized, will vary witheach system. Suitable phase diagram curves for several systems havealready been developed. However, if an appropriate curve is notavailable, this can be readily developed by known techniques. Forexample, a suitable technique is set forth in Smolders, van Aartsen andSteenbergen. Kolloid--Z. u. Z. Polymere, 243, 14 1971).

A more general graph of temperature vs. concentration for a hypotheticalpolymer-liquid system is given by FIG. 1A. The portion of the curve fromγ to α represents thermodynamic equilibrium liquid-liquid phaseseparation. The portion of the curve from α to β represents equilibriumliquid-solid phase separation, which will be recognized as the normalfreezing point depression curve of a hypothetical liquid-polymer system.The upper shaded area represents an upper liquid/liquid immiscibilitywhich may be present in some systems. The dotted line represents thelowering of crystallization temperature as a consequence of cooling at arate sufficient to achieve thermodynamic non-equilibrium liquid-liquidphase separation. The flat portion of the crystallization vs.composition curve defines a useable composition range which is afunction of the cooling rate employed, as will be discussed in moredetail.

Thus, for any given cooling rate, one may plot the crystallizationtemperature vs. percentage resin or compatible liquid and in such amanner determine the liquid/polymer concentration ranges which willyield the desirable microporous structures at the given cooling rate.For crystalline polymers, the determination of the useable concentrationrange via the plotting of the aforementioned crystallization curve is aviable alternative to determining a phase diagram, as shown in FIG. 1.As an example of the foregoing, one may refer to FIG. 55 which is a plotof temperature vs. polymer/liquid concentration showing the melt curveat a heating rate of 16° C. per minute, and crystallization curve forpolypropylene and quinoline over a broad concentration range. As may beseen by reference to the crystallization curve, at a cooling rate of 16°C. per minute, the appropriate concentration range extends from about 20percent polypropylene to about 70 percent polypropylene.

FIG. 56 is a graph of temperature versus polymer/liquid composition forpolypropylene and N,N-bis(2-hydroxyethyl)tallowamine. The upper curve isa plot of the melt curve at a heating rate of 16° C. per minute. Thelower curves, in descending order, are plots of the crystallizationcurves at cooling rates of 8° C., 16° C., 32° C., and 64° C., perminute. The curves demonstrate two concurrent phenomena which occur whenthe cooling rate is increased. First, the flat portion of the curvedemonstrating a relative stable temperature of crystallization across abroad concentration range, is lowered with increased cooling rateshowing that the faster the rate of cooling, the lower the actualcrystallization temperature.

The second observable phenomenon is the change in the slope of thecrystallization curve which occurs with changes in the rate of cooling.Thus, it appears that the flat region of the crystallization curve isexpanded when the cooling rate is increased. Accordingly, one may assumethat by increasing the rate of cooling, one may correspondingly increasethe operable concentration range for forming the microporous structuresof the present invention and for practicing the processes of the instantinvention. From the foregoing it is apparent that to determine theoperable concentration ranges for a given system, one need only preparea few representative concentrations of polymer/liquid and cool the sameat some desired rate. After the crystallization temperatures have beenplotted, the operable range of concentrations will be quite apparent.

FIG. 57 is a graph of temperature versus polymer/liquid concentrationfor polypropylene and dioctyl phthalate. The upper curve represents themelt curve for the system over a range of concentrations and the lowercurve represents the crystallization curve over the same concentrationrange. As the crystallization curve does not exhibit any flat regionover which the crystallization temperature remains substantiallyconstant for a range of concentrations, one would not expect thepolypropylene/dioctyl phthalate system to be capable of formingmicroporous structures, and, indeed, it does not.

To appreciate the excellent correlation between the phase diagram methodof determining operable concentration ranges of polymer and liquid andthe crystallization method of making such a determination, one may referto FIGS. 58 and 59. FIG. 58 is a phase diagram for a low molecularweight polyethylene and diphenyl ether polymer/liquid system, determinedby a conventional light scattering technique utilizing a thermallycontrolled vessel. From the phase diagram of FIG. 58, it appears thatT_(m) is at about 135° C. and φ_(m) is at about 7 percent polymer.Furthermore, it is apparent that at about 45 percent polymerconcentration, the cloud point curve intersects the freezing pointdepression curve, thus indicating an operable concentration range ofabout 7 percent polymer to about 45 percent polymer.

One may compare the operable range determined from FIG. 58 to the rangedeterminable from FIG. 59 which shows melt curves of the same system atheating rates of 8° C. and 16° C./minute and crystallization curves forsaid system at cooling rates of 8° C. and 16° C./minute. From thecrystallization curves it appears that the substantially flat portionthereof extends from somewhat below 10 percent polymer concentration toapproximately 42-45 percent polymer, depending on the cooling rate.Thus, the results obtained from the crystallization curves agreesurprisingly well with the results obtained from the cloud point phasediagram.

For non-crystalline polymers it is believed that one may refer to atemperature vs. concentration plot of the glass transition temperature,as an alternative to referring to a phase diagram such as that ofFIG. 1. Thus, FIG. 60 is a graph of temperature vs. concentration forthe glass transition temperature of low molecular weight polystyrene,supplied by Pennsylvania Industrial Chemical Corporation under thedesignation Piccolastic D-125, and 1-dodecanol, at various concentrationlevels.

From FIG. 60 it is apparent that from about 8 percent polymer to about50 percent polymer, the glass transition temperature for thepolystyrene/1-dodecanol is essentially constant. It has therefore beenproposed that the concentrations along the substantially flat portion ofthe glass transition curve would be operable in the practice of theinstant invention, analagous to the flat portion of the crystallizationcurves previously discussed. It thus appears that a viable alternativeto determining the phase diagram for non-crystalline polymer systems isto determine the glass transition curve and to operate in thesubstantially flat region of such a curve.

In all of the foregoing FIGs., the crystallization temperatures weredetermined with a DSC-2, differential scanning calorimeter, manufacturedby Perkin-Elmer, or comparable equipment. Further effects of coolingrates as the practice on the present invention will be discussedhereinbelow.

After one has chosen the desired synthetic thermoplastic polymer, thecompatible liquid and the potentially operable concentration range, oneneeds to choose, for example, the actual concentration of polymer andliquid which will be utilized. In addition to considering, for example,the theoretically possible concentration range, other functionalconsiderations should be employed in determining the proportions usedfor a particular system. Thus, insofar as the maximum amount of liquidwhich should be utilized is concerned, the resulting strengthcharacteristics must be taken into account. More particularly, theamount of liquid used should accordingly allow the resulting microporousstructure to have sufficient minimum "handling strength" to avoidcollapse of the microporous or cellular structure. On the other hand,the selection of the maximum amount of resin, viscosity limitations ofthe particular equipment utilized may dictate the tolerable maximumpolymer or resin content. Moreover, the amount of polymer used shouldnot be so great as to result in closing off the cells or other areas ofmicroporosity.

The relative amount of liquid used will also, to some extent, bedependent upon the desired effective size of the microporosity, as, forexample, the particular cell and pore size requirements of the ultimateapplication involved. Thus, for example, the average cell and pore sizetend to increase somewhat with increasing liquid content.

In any event, the utility of a liquid and the operable concentrationthereof, for a particular polymer, can be readily determined byexperimentally using the liquid as has seen described.

The parameters previously discussed should, of course, be followed.Indeed, as should be appreciated, blends of two or more liquids can beused; and the utility of a particular blend can be ascertained asdescribed herein. Also, while a particular blend may be useful, one ormore of the liquids may conceivably be unsuitable individually.

As may be appreciated, the particular amount of liquid employed willlikewise be often dictated by the particular end use application. Asillustrative examples of specific examples, utilizing high densitypolyethylene and N,N-bis(2-hydroxyethyl)talloamine, useful microporousproducts can be made by utilizing, by weight, from about 30 to about 90%amine, 30 to 70 being preferred. With low density polyethylene and thesame amine, the amount of liquid can usefully be varied within the rangefrom about 20 to 90%, 20 to 80 being preferred. In contrast, whendiphenylether is used as the liquid, useful low density polyethylenesystems contain no more than about 80% of the liquid, a maximum of about60% being preferred. When 1-hexadecene is used with low densitypolyethylene, amounts up to about 90% or more may be readily utilized.When polypropylene is used with the tallowamine previously described,the amine may be suitable employed in amounts of from about 10 to 90%,with a maximum amount of no more than about 85% being preferred. Withpolystyrene and 1-dodecanol, the concentration of the alcohol can varyfrom about 20 to about 90%, with from about 30 to about 70% beingpreferred. When styrene-butadiene copolymers are employed, the aminecontent may range from about 20 to about 90%. When a decanol andstyrene-butadiene copolymer (i.e. -SBR) system is used, the liquidcontent can suitably vary from about 40 to about 90%; withdiphenylamine, the liquid content is suitable within the range of fromabout 50 to about 80%. When microporous polymers are formed from theamine and an ethylene-acrylic acid copolymer, the liquid content mayvary within the range of from about 30 to about 70%; with diphenylether, the liquid content may vary from about 10 to about 90%, as is thecase when dibutylphthalate is used as the solvent.

SHAPING OF THE HOMOGENEOUS LIQUID

Following the formation of the solution, the same may then be processedto provide any desired shape or configuration. In general, and dependingupon the particular system involved, the thickness of the article canvary from a thin film of about 1 mil. or less up to a relatively thickblock of thickness of about 21/2 inches or even more. The ability toform blocks thus allows the microporous material to be processed intoany desired intricate shape, as by using conventional extrusion,injection molding or other related techniques. The practicalconsiderations involved in determining the range of thicknesses whichcan be made from a particular system include the rate of viscositybuild-up which the system undergoes as it cools. Generally, the higherthe viscosity, the thicker the structure can be. The structure canaccordingly be of any thickness so long as gross phase separation doesnot occur, i.e.--2 discernible layers become visually apparent.

It will be appreciated that if liquid-liquid phase separation is allowedto take place under thermodynamic equilibrium conditions the result willbe a complete separation into two distinct layers. One layer consistingof molten polymer containing the soluble amount of liquid and a liquidlayer containing the soluble amount of polymer in the liquid. Thiscondition is represented by the binodial line in the phase diagram inFIGS. 1 and 1A. It is apparent that a limitation as to the size ofobject which may be prepared is governed by the heat transfercharacteristics of the composition for if the object is thick enough andthe heat transfer is poor enough the rate of cooling in the center ofthe object may be slow enough to approach thermodynamic equilibriumconditions and result in a distinct layer phase separation as previouslydescribed.

Increased thicknesses may also be achieved by the addition of minoramounts of thixotropic materials. For example, the addition ofcommercially available colloidal silica prior to cooling significantlyincreases useful thicknesses yet does not adversely affect thecharacteristic microporous structure. The particular amounts to be usedcan be readily determined.

COOLING OF THE HOMOGENEOUS SOLUTION

As is apparent from the above discussion, regardless of the type ofprocessing (e.g.--casting into a film or the like), the solution must becooled down to form what behaves as, and appears as, a solid. Theresulting material should have sufficient integrity so that it will notcrumble upon handling, as in one's hand. A further test to ascertainwhether the requisite system possesses the desired structure is toemploy a solvent for the liquid employed but not for the polymer. If thematerial disintegrates, the system employed did not satisfy thenecessary criteria.

The rate of cooling of the solution may be varied within wide limits.Indeed, in the usual case, no external cooling need be employed, and itis satisfactory merely to, for example, cast a film by pouring the hotliquid system onto a metallic surface heated to a temperature whichallows the drawing of the film or, alternatively, forming a block bypouring onto a substrate at ambient conditions.

The rate of cooling, as previously discussed must be sufficiently fastso that the liquid-liquid phase separation does not occur underthermodynamic equilibrium conditions. Furthermore, the rate of coolingmay have substantial effect upon the resultant microporous structure.For many polymer/liquid systems, if the rate of cooling is sufficientlyslow, but still satisfying the aforementioned criteria, then theliquid-liquid phase separation will result at substantially the sametime in the formation of a plurality of liquid droplets of substantiallythe same size. If the cooling rate is such that the plurality of liquiddroplets does form, as long as all other conditions discussed hereinhave been satisfied, the resultant microporous polymer will have thecellular microstructure, as previously defined.

In general, it is believed that the unique structures of the microporouspolymers of the present invention are obtained by cooling the liquidsystem to a temperature below the binodial curve, as shown in FIG. 1, sothat liquid-liquid phase separation is initiated. At this state, nucleiwill begin to form, consisting principally of pure solvent. When therate of cooling is such that the cellular microstructure results, it isalso believed that as each such nucleus continues to grow, it becomessurrounded by a polymer-rich region which increases in thickness as itbecomes depleted of liquid. Eventually, this polymer-rich regionresembles a skin or film covering the growing droplet of solvent. As thepolymer-rich region continues to thicken, the diffusion of additionalsolvent through the skin decreases; and the growth of the liquid dropletcorrespondingly decreases until it effectively stops, the liquid droplethaving reached its maximum size. At this point, the formation of a newnucleus is more probable than continued growth of the large solventdroplet. However, to achieve this mode of growth, it is necessary thatnucleation be initiated by spinodal decomposition rather than bybinodial decomposition.

The cooling is thus carried out in such a fashion as to form atsubstantially the same time a plurality of liquid droplets ofsubstantially the same size in a continuous polymer phase. If thisdecomposition mode does not take place, the cellular structure will notresult. The appropriate decomposition mode is achieved, in general, byemploying conditions which ensure that the system does not achievethermodynamic equilibrium until at least the nucleation or dropletgrowth has been initiated. Process-wise, this can be accomplished bymerely allowing the system to cool without subjecting it to mixing orother shear forces. The time parameter may also be significant whererelatively thick blocks are being formed, making more rapid coolingdesirable in such instances.

Within the range over which cooling results in the formation of aplurality of liquid droplets, there is a general indication that therate of cooling may affect the size of the resulting cells, withincreasing rates of cooling resulting in smaller cells. In thisconnection, it has been observed that an increase in the cooling ratefrom about 8° C./minute will apparently result in decreasing the cellsize in half for a polypropylene microporous polymer. Accordingly,external cooling may be utilized, if desired, to control the ultimatecell and pore size, as will be discussed in more detail.

The manner in which the interconnecting passageways or pores are formedin the cellular structure is not fully understood. However, and whilethe applicant does not wish to be bound by any particular theory thereare various possible mechanisms that serve to explain this phenomenon,each of which is consistent with the concept described herein. Theformation of the pores may accordingly be due to thermal shrinkage ofthe polymer phase upon cooling, the liquid solvent droplets behaving asincompressible spheres when the solvent has a smaller expansioncoefficient than the polymer. Alternatively, and as has been pointedout, even after the solvent droplets have reached their maximum size,the polymer-rich phase will still contain some residual solvent and viceversa. When the system continues to cool, additional phase separationmay accordingly occur. The residual solvent in the polymer-rich skin cantherefore diffuse to the solvent droplet, reducing the volume of thepolymer-rich skin and increasing the volume of the solvent droplet.Conceptually, this may weaken the polymer skin; and the volume increaseof the solvent or liquid phase may result in internal pressure which iscapable of bursting through the polymer skin, connecting adjacentsolvent droplets. Related to this last mechanism, the polymer mayredistribute itself into a more compact state as the residual liquidmigrates out of the polymer skin, as by crystallization when this typeof polymer is employed. In such a situation, the resulting polymer skinwould likely shrink and have imperfections or apertures, likely locatedin the areas of particular weakness. The weakness areas would, it can beexpected, be located between adjacent liquid droplets; and, in such asituation, the apertures would form between adjacent liquid droplets andresult in the interconnection of the solvent droplets. At any rate, andregardless of the mechanism, the interconnecting pores or passagewaysinherently result when the process is carried out as has been describedherein.

An alternative explanation of the mechanism by which the pores areformed is based on the "Marangoni effect", which has been discussed inMarangoni, C, Nuovo Cimento [2] 5-6.239 (1871), [3], 3,97,193 (1878) andMarangoni, C. Ann. Phys. Lpz. (1871), 143,337. The Marangoni effect hasbeen utilized to explain the phenomenon occurring when alcoholicbeverages spontaneously reflux off the sides of drinking glasses,particularly, the mechanism occurring when a condensed droplet flowsback into the bulk of the liquid. The fluid of the droplet firstpenetrates that of the bulk, followed by the rapid retreat of part ofthe fluid back into the droplet. In has been hypothesized that a similarphysical phenomenon is occurring with the liquid droplets which haveformed as a result of the liquid-liquid phase separation. Thus, onedroplet may encounter another and the fluid of one may penetrate that ofthe other, followed by rapid separation of the two droplets, perhapsthen leaving a portion of the liquid connecting the two droplets andforming the basis for the interconnecting pores of the cellularstructure. For a more recent discussion of the Marangoni effect, one mayrefer to Charles & Mason, J. Colloid Sc:, 15, 236-267 (1960).

If the cooling of the homogeneous solution occurs at a sufficiently fastrate, liquid-liquid phase separation may occur under non-equilibriumthermodynamic conditions, but substantial solidification of the polymermay occur so rapidly that essentially no nucleation and subsequentgrowth may occur. In such an instance there will be no formation of aplurality of liquid droplets and the resulting microporous polymer willnot have the distinct cellular structure.

Thus, under some circumstances it is possible to obtain differentmicroporous structures by use of exceptionally high cooling rates. Forexample, when a solution of 75 parts ofN,N-bis(2-hydroxyethyl)tallowamine and 25 parts of polypropylene iscooled at rates varying from about 5° C. to about 1350° C. per minute,the cellular microstructure results. The main effect of differentcooling rates in the foregoing range on the composition is thealteration of the absolute cell size. Where cooling rates of about 2000°C./minute are achieved, the microstructures take on, for example, a finelacey, non-cellular appearance. When a solution of 60 parts ofN,N-bis(2-hydroxyethyl)tallowamine and 40 parts of polypropylene aretreated in the same fashion, cooling rates in excess of 2000° C. perminute must be achieved before the lacey non-cellular structure isobtained.

To investigate the effect of cooling system rate on the cell size of thecellular structure and to investigate the rate of cooling necessary fortransition from production of the cellular structure to production of astructure having no distinct cells, various concentration ofpolypropylene and N,N-bis(2-hydroxyethyl)tallowamine were prepared ashomogeneous solutions. To accomplish such an investigation, the DSC-2,previously discussed, was utilized in conjunction with standard X-rayequipment, and a scanning electron microscope. As the DSC-2 is capableof a maximum cooling rate of about 80° C./minute, a thermal gradient barwas also utilized. The thermal gradient bar was a brass bar which wascapable of having a temperature differential of greater then 2000° C.across its one meter length, upon which samples could be placed.

An infrared camera was utilized to determine the temperatures of thesamples by first focusing the camera on a pan which was placed in theclosest of the ten bar sites to a temperature of 110° C., as measuredwith a thermocouple. The camera emissivity control was then adjusteduntil the camera temperature readout agreed with the thermocouplereading.

For any given run, the camera was focused on a location at which a givenpan containing the sample solution was to cool. The pan with the samplewas then placed on the thermal gradient bar for two minutes. As the panwas removed from the bar to be placed in the field of the camera, astopwatch was started. As soon as the camera indicated that the pan wasat a temperature of 110° C., the stopwatch was stopped and the timerecorded. Thus, the determined cooling rates were based on the timeneeded for the sample to cool over a temperature range of approximately100° C.

It was found that the controlling limitation on the rate of cooling wasnot the amount of material being cooled. It was noted that althoughheavier samples cooled more slowly than light ones, the silicon oilwhich was used on the bottom of the pan for thermal conductivity betweenthe pan and bar had significant influence on the rate of cooling. Thusthe highest cooling rates were obtained by placing a pan without anysilicon oil on an ice cube and the slowest cooling rates were obtainedwith a pan having a heavy coating of silicon oil which was placed onto apiece of paper.

Five samples of polypropylene were prepared containing from 0 percentN,N-bis(2-hydroxyethyl)tallowamine to 80 percent of said amine, for usein investigating the effect of cooling rate on the resultant structures.Approximately 5 milligrams of each of said samples were heated on theDSC-2 inside of sealed pans at 40° C. per minute to a holdingtemperature of 175° C. for the sample containing 20 percentpolypropylene, 230° C. for the sample containing 40 percentpolypropylene, 245° C. for the sample containing 60 percentpolypropylene, 265° C. for the sample containing 80 percentpolypropylene and 250° C. for the 100 percent polypropylene.

Each of the samples were heated to and maintained at the appropriateholding temperature for five minutes prior to being cooled. After thesamples were cooled at the desired cooling rate, theN,N-bis(2-hydroxyethyl)tallowamine was extracted from the sample withmethanol and the sample analyzed. The results of the study aresummarized in TABLE I showing the sizes of the cells in microns, in theresulting compositions. All cell sizes were determined by makingmeasurements from the respective scanning electron micrographs.

                  TABLE I                                                         ______________________________________                                               Cooling Rate                                                           Composition                                                                            5° C./Min.                                                                       20° C./Min.                                                                      40° C./Min.                                                                    80° C./Min.                       ______________________________________                                         0% Amine                                                                              None.sup.(1)                                                                            None.sup.(1)                                                                            None.sup.(1)                                                                          None.sup.(1)                             20% Amine                                                                              0.5.sup.(2)                                                                             0.5.sup.(2)                                                                             None.sup.(3)                                                                          None.sup.(3)                             40% Amine                                                                              2.5.sup.(4)                                                                             2.0.sup.(4)                                                                             2.0.sup.(4)                                                                           0.7.sup.(5)                              60% Amine                                                                              4.0       3.0       2.0     1.5.sup.(6)                              80% Amine                                                                              0.5       4.0       3.0     3.0.sup.(6)                              ______________________________________                                         .sup.(1) Some irregular holes present                                         .sup.(2) Approximation of largest cell                                        .sup.(3) Porosity probably too small to                                       .sup.(4) Some small cells present at 1/10 size of larger                      .sup.(5) Additional cells present too small to                                .sup.(6) Some formation of noncellular structure                         

An additional cooling rate study was conducted utilizing samples of 20percent polypropylene and 80 percent N,N-bis(2-hydroxyethyl)tallowaminetallowamine on the thermal gradient bar. Five of such samples werecooled at various rates from a melt temperature of 210° C. and theresults are summarized in TABLE II, showing the sizes of the cells inmicrons, the same procedure being utilized as for obtaining the data forTABLE I.

                  TABLE II                                                        ______________________________________                                        Compo-  Cooling Rate                                                          sition  200° C.                                                                        870° C./Min.                                                                      1350° C./Min.                                                                   1700° C./Min.                      ______________________________________                                        80% Amine                                                                             0.5-3   0.5-1.5    1.5-2.5  Non-cellular                              ______________________________________                                    

From TABLES I and II it is apparent that for increasing cooling rates,the size of the cells in the resulting compositions decrease, ingeneral. Furthermore, with respect to the polymer/liquid systemcomprised of 20 percent polypropylene and 80 percentN,N-bis(2-hydroxyethyl)tallowamine, it is apparent that at a coolingrate between about 1350° C. per minute and 1700° C. per minute atransition is completed in the nature of the resultant polymer fromessentially cellular to non-cellular. Such a transition in the resultantstructure corresponds to the fact that the polymer becomes substantiallysolidified after liquid-liquid phase separation has been initiated butprior to the formation of a plurality of liquid droplets, as previouslydiscussed.

Additionally five samples of 40 percent polypropylene and 60 percentN,N-bis(2-hydroxyethyl)tallowamine were prepared and cooled at ratesfrom 690° C. per minute to over 7000° C. per minute, from melttemperatures of 235° C., in accordance with the procedure discussedpreviously. It was determined that for such a concentration ofpolypropylene and said amine, the transition from cellular tonon-cellular occurs at about 2000° C. per minute.

Finally, to investigate the crystallinity of structures prepared over arange of cooling rates, three samples of 20 percent polypropylene and 80percent N,N-bis(2-hydroxyethyl)tallowamine were prepared and cooled atrates of 20° C., 1900° C. and 6500° C. per minute. From the DSC-2 datafor such samples it was determined that the degree of crystallinity inthe three samples was essentially equivalent. Thus it appears thatvariations in the cooling rate have no significant effect upon thedegree of crystallinity of the resulting structures. However, it wasdetermined that as the rate of cooling was significantly increased, thecrystals which were produced became less perfect, as expected.

REMOVAL OF THE LIQUID

Having formed the homogeneous solution of polymer and liquid and havingcooled the solution in an appropriate manner to produce a materialhaving suitable handling strength, the microporous product may bethereafter formed by removing the liquid by, for example, extractingwith any suitable solvent for the liquid which is, likewise, quiteobviously, a non-solvent for the polymer in the system. The relativemiscibility or solubility of the liquid in the solvent being employedwill, in part, determine the effectiveness in terms of the time requiredfor extraction. Also, if desired, the extracting or leaching operationcan be carried out at an elevated temperature below the softening pointof the polymer to lessen the time requirements. Illustrative examples ofuseful solvents include isopropanol, methylethyl ketone,tetrahydrofuran, ethanol and heptane.

The time required will vary, depending upon the liquid employed, thetemperature used and the degree of extraction required. Moreparticularly, in some instance, it may be unnecessary to extract 100% ofthe liquid used in the system and minor amounts may be tolerated, theamount which can be tolerated being dependent upon the requirements ofthe intended end-use application. The time required may accordingly varyanywhere in the range of from several minutes or perhaps less to morethan 24 hours or even more, depending upon many factors, including thesample thickness.

Removal of the liquid can also be achieved by other known techniques.Illustrative examples of other useful removal techniques includeevaporation, sublimation and displacement.

It should be noted in addition, when using conventional liquidextraction techniques, the cellular microporous polymer structures ofthe present invention may exhibit release of a liquid contained in thestructure in a fashion which approaches zero order, i.e., the rate ofrelease may be essentially constant after, perhaps, an initial period ata high release rate. In other words, the rate of release may beindependent of the amount of the liquid that has been released; thus,the rate at which the liquid is extracted after, for example,three-fourths of the liquid has been removed from the structure isapproximately the same as when the structure was one-half filled withliquid. An example of such a system exhibiting an essentially constantrelease rate is the extraction of N,N-bis-(2-hydroxyethyl)tallowaminefrom polypropylene with isopropanol as the extractant. Also, in anysituation, there probably will be an initial induction period before therate of release becomes identifiable. When release of a liquid isallowed to proceed by evaporation, the rate of release tends to be firstorder.

CHARACTERIZATION OF THE MICROPOROUS POLYMERS CELLULAR STRUCTURE

When the cooling of the polymer/liquid solution occurs such that theplurality of liquid droplets form as previously discussed, and theliquid removed therefrom, the resulting microporous product forms arelatively homogeneous cellular structure comprising, on the microscale,a series of substantially spherical, enclosed microcells distributedsubstantially uniformly throughout the structure. Adjacent cells areinterconnected by smaller pores or passageways. This basic structure canbe seen from the photomicrographs of FIGS. 4 and 5. It should beappreciated that the individual cells are, in fact, enclosed but appearopen in the photomicrographs due to the fracturing involved in thesample preparation for taking the photomicrographs. On a macroscale, atleast for the crystalline polymers, the structure appears to have planessimilar to the fracture planes along the edges of crystal growth (seeFIG. 2) and, as can be seen from FIG. 3, is coral-like in appearance.The cellular microstructure may further be analogized to zeolite claystructures, which contain definite "chamber" and "portal" regions. Thecells correspond to the larger chamber areas of zeolite structures whilethe pores correspond to the portal regions.

In general, in the cellular structure the average diameter of the cellswill vary from about 1/2 micron to about 100 microns, about 1/2 to about50 microns being more typical whereas the average diameter of the poresor interconnecting passageways appears to be typically about a magnitudesmaller. Thus, for example, if the cell diameter in a microporouspolymer structure of the present invention is about 1 micron, theaverage diameter of the pore or interconnecting passageway will be about0.1 micron. As has been pointed out previously, the cell diameter andalso the diameter of the pore or passageway will be dependent upon theparticular polymer-liquid system involved, the rate of cooling and therelative amounts of polymer and liquid utilized. However, a broad rangeof cell to pore ratios are possible, as, for example, from about 2:1 toabout 200:1, typically, from about 5:1 to about 40:1.

As can be seen from the several Figures, it may be considered that someof the exemplary cellular microporous polymer products do not possessthe unique microcellular structure which has been described herein. Itmust, however, be appreciated that this structure can, in someinstances, be masked by additional modifications resulting from theparticular liquid or polymer involved or the relative amounts employed.This masking may be in whole or in part, ranging from small polymerparticles attached to the walls of the cells to gross "foliage-type"polymer build-ups which, in the micrographs, tend to completely mask thebasic structure. Thus, for example, and as can be seen from FIGS. 21 and25, small polymer balls are adhered to the cell cavities of thestructures. This additional formation can be understood by reference tothe nucleation and growth concept previously described. Thus, in systemswith extremely high solvent or liquid content, the maximum cavity sizewill typically be comparatively large. This likewise means that the timerequired for the cavity or droplet to reach its maximum size willsimilarly be increased. During this time, it is possible for additionalnuclei to form nearby. Two or more nuclei may then come into contactwith one another prior to each reaching its maximum size. In suchinstances, the resulting cellular structure has less integrity andsomewhat less regularity than the basic structure previously described.Moreover, even after the liquid droplets have reached maximum size,depending upon the system involved, the solvent or liquid phase maystill contain some amount of residual polymer or vice versa. In suchsituations, as the system continues to cool, some additional residualphase separation may occur. When the residual polymer simply separatesout of solution, spheres of polymer can form as shown in FIGS. 21 and25. On the other hand, if the residual polymer diffuses to the polymerskin, the walls will appear fuzzy and irregular, thus providing the"foliage-type" structure. This "foliage-type" structure may onlypartially mask the basic structure, as seen in FIGS. 28 and 29 or it maywholly mask the structure as shown in FIG. 6.

The "foliage-type" structure is also more prone to occur with certainpolymers. Thus, the microporous low density polyethylene structures,perhaps due to the solubility or the like of the polyethylene in theparticular liquids employed, typically provide this sort of structure.This can be observed from FIG. 14. Further, when the levels of liquidemployed are extremely high, this will also occur with polymers such aspolypropylene which otherwise exhibit the basic structure. This can bereadily observed by contrasting the "foliage-type" structure of themicroporous product of FIG. 6 with the basic structure of FIG. 8 inwhich the polymer content is 40% by weight compared to the 10%polypropylene in the structure illustrated in FIG. 6.

For most applications, it is preferred to utilize a system which resultsin the formation of the basic cellular structure. The relativehomogeneity and regularity of this structure provides predictableresults, such as are required in filtration applications. However, thefoliage-type structure may be more desirable where relatively highsurface area structures are desired such as in ion exchange or variousadsorptive processes.

As can be likewise observed, some of the structures have small holes orapertures in the walls of the cells. This phenomenon can also beunderstood by reference to the nucleation and growth concept. Thus, in asection of the system in which a few spatially associated liquiddroplets have already reached their maximum size, each droplet will beenclosed by a polymer-rich skin. However, in some instances, somesolvent may be trapped between the enclosed droplets but cannot continueits migration to the larger droplets due to impenetrability of theskins. Accordingly, in such instances, a nucleus of the liquid may formand grow, resulting in a small cavity embedded adjacent to the largerdroplets. After extraction of the liquid, the smaller droplets willappear as a small hole or aperture. This can be observed in themicroporous structures shown in FIGS. 11-12 and 20.

Another interesting characteristic of the cellular structures of thepresent invention relates to the surface area of such structures.

The theoretical surface area of the cellular microporous structureconsisting of interconnected spherical cavities of about 5 microns indiameter is approximately 2-4 sq meters/gm. It has been found thatmicroporous polymers produced by the instant invention need not belimited to the theoretical limit of surface area. Determination ofsurface area by the B.E.T. method described in Brunauer, S., Emmett, P.H. and Teller, E. "The Adsorption of Gases in Multimolecular Layers" J.Am. Chem. Soc., 60, 309,-16 (1938), has shown surface surface areas farin excess of the theoretical model which is not related to the voidspace, as shown in Table III, for microporous polymers made frompolypropylene and N,N-bis(2-hydroxyethyl)tallowamine.

                  TABLE III                                                       ______________________________________                                        % VOID        SPECIFIC SURFACE AREA                                           ______________________________________                                        89.7          96.2       m.sup.2 /gm                                          72.7          95.5                                                            60.1          98.0                                                            50.5          99.8                                                            28.9          88.5                                                            ______________________________________                                    

Surface area may be reduced by careful annealing of the microporouspolymer without affecting the basic structure. Microporous polypropyleneprepared at 75% void space using N,N-bis(2-hydroxyethyl)tallowamine asthe liquid component was extracted and dried at temperatures notexceeding room temperature and subsequently heated to affect the surfacearea. The initial surface area was 96.9 m² /g. After eleven 40 minuteheat periods at 62° C. the surface area fell to 66 m² /gm. Furtherheating at 60° C. for an additional 66 hours decreased the surface areato 51.4 m² /gm. Treatment of another sample at 90° C. for 52 hoursdecreased the surface area from 96.9 to 33.7 m² /gm. The microporousstructure was not significantly changed when examined by scanningelectron microscopy. These results are summarized in Table IV.

                  TABLE IV                                                        ______________________________________                                        Treatment   Surface area (m.sup.2 /gm)                                                                       % Change                                       ______________________________________                                        none        96.9               --                                             eleven, 40 min.                                                               treatments at 62° C.                                                               66.0               32%                                            Above plus 66 hours                                                           at 60° C.                                                                          51.4               47%                                            52 hours at 90° C.                                                                 33.7               65%                                            ______________________________________                                    

It should be quite apparent that one of the unique features of thecellular structures of the present invention relates to the existence ofboth distinct, substantially spherical, enclosed microcells which areuniformly distributed throughout the structure and distinct pores whichinterconnect said cells, said pores being of a smaller diameter thansaid cells. Furthermore, said cells and interconnecting pores haveessentially no spatial orientation, and may be classified as beingisotropic. Thus there is no preferred direction, as for example, forflow of a liquid through the structure. This is in marked contrast toprior art materials which do not exhibit such a cellular structure. Manyprior art systems have a nondescript structure which lacks anystructural configuration capable of definition. It is therefore quitesurprising that a microporous structure can be made having such a degreeof uniformity, which may be especially desirable for many applicationsneeding highly uniform materials.

The cellular structure may be defined in terms of the ratio of theaverage diameter of the cells ("C") to the diameter of the pores ("P").Thus, the C/P ratio as previously discussed may vary from about 2 toabout 200, about 5 to about 100 being typical and about 5 to about 40being even more typical. Such a C/P ratio distinguishes the cellularstructure of the present invention from any previous prior artmicroporous polymeric product. As there is no known prior art syntheticthermoplastic polymeric structure having distinct cells and pores, allsuch prior art materials must be considered to have a cell to pore ratioof 1.

Another means of characterizing the cellular structures of the presentinvention is by a sharpness Factor, "S". The S factor is determined byanalyzing a mercury intrusion curve for the given structure. All mercuryintrusion data discussed in this application was determined by use of aMicromeritics Mercury Penetration Porosimeter, Model 910 series. The Svalue is defined as the ratio of the pressure at which 85 percent of themercury penetrated to the pressure at which 15 percent of the mercurypenetrated. This ratio is a direct indication of the variation in porediameter across the central 70 percent of the pores in any given sample,as pore diameter is equal to 176.8 divided by the pressure in p.s.i.

The S value, then, is a ratio of the diameter of the pores at which 15percent of the mercury has intruded to the diameter of the pores atwhich 85 percent of the mercury has intruded. The range for 1 to 15percent and 85 to 100 percent of mercury intrusion is ignored indetermining the S factor. The range from 0 to 15 percent is ignored aspenetration in this range may be due to cracks introduced into thematerial as a result of the freeze-fracturing to which the material wassubjected prior to performing the mercury intrusion study. Also, therange from 85 to 100 percent is ignored as data in such a range may bedue to compression of the sample rather than to actual penetration ofthe mercury into the pores.

Characteristic of the narrow range of pore sizes exhibited by thecomposition of the present invention, the usual S value for suchstructures is in the range of from about 1 to about 30, about 2 to about20 being typical and about 2 to about 10 being more typical.

The average size of the cells in the structure range from about 0.5 toabout 100 microns, from about 1 to about 30 microns being typical, fromabout 1 to about 20 microns being more typical. As indicated the cellsize may vary depending on the particular resin and compatible liquidutilized, the ratio of polymer to liquid, and the cooling rate employedto form the particular microporous polymer. The same variable will alsohave an effect upon the average size of the pores in the resultingstructure, which usually varies from about 0.05 to about 10 microns,from about 0.1 to about 5 microns being typical, and from about 0.1 toabout 1.0 micron being more typical. All references to a cell and/orpore size throughout this application, relate to the average diameter ofsuch cell or pore, in microns, unless otherwise stated.

By determining the foregoing factors, cell size, pore size, and S, forthe cellular microporous polymers of the present invention, one mayconcisely define the cellular microporous polymers of the presentinvention. A particularly useful means of so defining the polymers interms of the log of the cell to pore ratio ("log C/P") and the log ofthe ratio of the sharpness function S to the cell size ("log S/C").Accordingly, the cellular microporous polymers of the present inventionhave a log C/P of from about 0.2 to about 2.4 and a log S/C of fromabout -1.4 to about 1.0, more usually, said polymers have a log C/P offrom about 0.6 to about 2.2 and a log S/C of from about -0.6 to about0.4.

Non-cellular Structure

The non-cellular structure of the present invention which results fromthe cooling of the homogeneous solution at such a rate that the polymersubstantially solidifies prior to the formation of the plurality ofliquid droplets, may be characterized primarily with respect to thenarrow pore size distribution of the material in conjunction with theactual pore size and the spatial uniformity of the structure.

Particularly, the non-cellular microporous polymers may be characterizedby a sharpness function, S, as previously described with respect to thecellular structures. The S values exhibited by the non-cellularstructure range from about 1 to about 30, about 1 to about 10 beingpreferred and about 6 to about 9 being more preferred. However, when thepore size of the material ranges from about 0.2 to about 5 microns, theS value will range from about 5 to about 10 and will typically rangefrom about 5 to about 10. Such S values for olefinic and oxidationpolymers having microporosity of such a size has been unknownheretofore, except in the case of highly oriented, thin films made by astretching technique. As previously indicated, the porous polymers ofthe present invention are substantially isotropic. Thus a cross-sectionof the polymers taken along any spatial plane will reveal essentiallythe same structural features.

The pore sizes of the non-cellular structures of the present inventionare usually in the range from about 0.05 to about 5 microns, from about0.1 to about 5 microns being typical, and from about 0.2 to 1.0 micronbeing more typical.

It is apparent that a surprising feature of the present invention is theability to produce isotropic microporous structures from olefinic andoxidation polymers, with the structures having porosity in the rangefrom about 0.2 to about 5 microns and a sharpness value from about 1 toabout 10. It is especially surprising that such structures may be madein the form, not only of thin films, but also in the form of blocks andintricate shapes.

GENERAL

When forming a film or block by pouring onto a substrate such as metalplate, for example, the surface of the microporous polymer structure ofthe present invention which is in contact with the plate will comprise asurface skin that is non-cellular. The other surface, in contrast, istypically predominantly open. The thickness of the skin will varysomewhat in accordance with the particular system as well as theparticular process parameters employed. However, typically, thethickness of the skin is approximately equal to the thickness of asingle cell wall. Depending upon the particular conditions, the skin mayrange from one which is wholly impervious to the passage of liquids toone exhibiting some degree of liquid porosity.

If a solely cellular structure is desired for the ultimate application,the surface skin may be removed by any of several techniques. Asillustrative examples, the skin could be removed by employing any one ofseveral mechanical means such as abrading, puncturing the skin withneedles or fracturing the skin by passing the film or other structurethrough differential speed rollers. Alternatively, the skin could bereoved by microtoming. The skin may also be removed by chemical means,i.e.--by brief contact with a suitable solvent for the polymer.

For example, when a solution of polypropylene inN,N-bis(2-hydroxyethyl)tallowamine is continuously extruded as a thinfilm onto an endless stainless steel belt conveyor, application of asmall amount of liquid solvent upon the belt immediately prior to thesolution application zone will effectively remove the surface formed atthe solution-steel interface. Useful liquids are materials such asisoparaffinic hydrocarbons, decane, decalin, xylene and mixtures such asxylene-isopropanol and decalin-isopropanol.

However, for some end use applications, the presence of the skin willnot only not be a detriment but will be a necessary component. Forexample, as is known, ultrafiltration or other membrane-typeapplications utilize a thin, liquid impenetrable film. Accordingly, insuch applications, the microporous portion of the structure of thepresent invention would be particular utility as a support for thesurface skin which would be functioning membrane in such applications.Wholly cellular structures can also be directly prepared by varioustechniques. Thus, for example, the polymer-liquid system could beextruded into air or a liquid medium such as, for example, hexane.

The microporous polymer structures of the present invention, as has beenpreviously discussed, have cell and pore diameters with extremely narrowsize distributions which are indicative of the unique structures andtheir relative homogeneity. The narrow size distribution of the porediameters is apparent from mercury intrusion data, as can be seen fromFIGS. 30-33. The same general distribution is obtained regardless ofwhether the structure is in the form of a film (FIGS. 30-32) or a block(FIG. 33). The characteristic pore size disdistribution of themicroporous structure of the present invention is in marked contrast tothe significantly broader pore size distribution of prior microporouspolymer products achieved by prior processes, such as, for example,those set forth in U.S. Pat. Nos. 3,310,505 and 3,378,507, as will bediscussed in greater detail in connection with the Examples.

For any of the microporous polymers made in accordance with the presentinvention, the particular end use application will typically determinethe amount of void space and pore size reqirements. For example, forprefilter applications, the pore size will typically be above 0.5microns while, in ultrafiltration, the pore sizes should be less thanabout 0.1 micron.

In applications where the microporous structure serves, in effect, as areceptacle for a functionally useful liquid strength considerationsdictate the amount of void space where controlled release of thecontained functional liquid is involved. Similarly, in such cases, thepore size will be dictated by the rate of release desired, smaller poresizes tending to provide slower rates of release.

Where the microporous structure is to be utilized to convert a liquidpolymer additive such as a flame retardant to a solid, some minimumstrength is generally desired; but, consistent with this minimum, itwill typically be desired to utilize as much liquid as possible sincethe polymer serves merely as a receptacle or carrier.

MICROPOROUS POLYMERS CONTAINING FUNCTIONAL LIQUIDS

From the foregoing discussions it should be appreciated that inaccordance with one aspect of the present invention, microporousproducts containing a functionally useful liquid such as polymeradditive (e.g.--flame retardant) may be prepared which behave as, andmay be processed as, a solid. To this end, the resulting microporouspolymer may be reloaded with the desired functional liquid. This can beaccomplished by conventional absorption techniques, and the amount ofliquid taken up will be essentially the same as the amount of liquidused in forming the microporous polymer in the first instance. Anyuseful organic liquid may be employed so long as, of course, the liquidis not a solvent for the polymer, or otherwise attacks or degrades, thepolymer at the working temperature. The microporous products containingthe functionally useful liquid may be formed from or by usingmicroporous polymers having either the cellular or non-cellularstructure, as the matrix in which the liquid is incorporated.

Similarly, such microporous products can be prepared by a displacementtechnique. In accordance with this embodiment, the microporous polymerintermediate is first prepared; and the liquid is then displaced,whether with the desired functionally useful liquid or with anintermediate displacing liquid. In either case, rather than extractingthe liquid used in forming the microporous polymer intermediate, thedisplacement is carried out by conventional pressure or vacuumdisplacement or infusion techniques. Any functional or intermediatedisplacing liquid may be used which could be used as an extractingliquid to form the microporous polymer, i.e.--is a non-solvent for thepolymer yet has some solubility or miscibility with the liquid beingdisplaced. As is apparent, minor amounts of the displaced liquid orliquids may remain following displacement. The requirement of the enduse will typically dictate the extent of the displacement desired, thus,amounts of about 1 to about 10% by weight may be tolerated in someapplications. If required, multiple displacements and/or using liquidsthat can be readily removed by evaporation allows removal of essentiallyall of the liquid or liquids being displaced, i.e.--less than about 0.03or so weight percent of residual liquid can be achieved. From theeconomic standpoint, it will generally be desirable to utilize adisplacing liquid which has a boiling point sufficiently different fromthe liquid being displaced to allow recovery and reuse. For this reason,it may be desirable to utilize an intermediate displacing liquid.

As may also be apparent from the foregoing examples of usefulpolymer-liquid systems, a further method of preparing apolymer-functionally useful liquid material involves utilizing themicroporous polymer intermediate without further processing sincenumerous functionally useful liquids have been found to be operable asthe comparable liquid with particular polymers to form the solidmicroporous polymer intermediate. Thus, intermediates which behave assolids can be directly made with liquids useful as lubricants,surfactants, slip agents, moth repellents, pesticides, plasticizers,medicinals, fuel additives, polishing agents, stabilizers, insect andanimal repellents, fragrances, flame retardants, antioxidants, odormasking agents, antifogging agents, perfumes and the like. For example,with low density polyethylene, useful intermediates containing alubricant or a plasticizer may be provided by employing either analiphatic or aromatic ester having eight or more carbon atoms or anonaromatic hydrocarbon having nine or more carbon atoms. Usefulproducts containing a surfactant and/or wetting agent may be formed withlow density polyethylene by using a polyethoxylated aliphatic aminehaving eight or more carbon atoms or a nonionic surfactant. Withpolypropylene, surfactant-containing intermediates can be provided byutilizing diethoxylated aliphatic amines having eight or more carbonatoms. Polypropylene intermediates containing slip agents may beprepared by using a phenylmethyl polysiloxane while low densitypolyethylene slip agent intermediates are formed by employing analiphatic amide having twelve to twenty-one carbon atoms. Low densitypolyethylene fuel additive intermediates may be prepared by utilizing analiphatic amine having eight or more carbon atoms or an aliphaticdimethyl tertiary amine having twelve or more carbon atoms. The tertiaryamines may also form useful additive intermediates with methylpentenepolymers. High and low density polyethylene intermediates containing astabilizer can be formd by using an alkyl aryl phosphite.

Intermediates of low density polyethylene including an antifogging agentmay be provided by utilizing the glycerol mono or diester of a longchain fatty acid having at least ten carbon atoms. Intermediates havingflame retardants incorporated therein may be prepared with high and lowdensity polyethylene, polypropylene, and a polyphenyleneoxide--polystyrene blend by using a polyhalogenated aromatic hydrocarbonhaving at least four halogen atoms per molecule. Useful materialsshould, of course, be liquid at the phase separation temperature asdescribed herein. Other systems which have been found useful will beidentified in connection with the Examples presented hereinafter.

Furthermore, for polypropylene, high density polyethylene, and lowdensity polyethylene, certain classes of ketones which have been foundto be especially useful as animal repellants may be employed generallyin the practice of the present invention. Such ketones may includesaturated aliphatic ketones having from 7 to 19 carbon atoms,unsaturated aliphatic ketones having from 7 to 13 carbon atoms, 4-t-amylcyclohexanone, and 4-t-butyl cyclohexanone.

The following Examples are presented to more fully explain the presentinvention and are merely illustrative of the present invention and arenot intended as a limitation upon the scope thereof. Unless otherwiseindicated, all parts and percentages are by weight.

PREPARATION PROCEDURE

The porous polymer intermediates and the microporous polymers describedin the Examples presented hereinafter were prepared according to thefollowing procedure:

A. Porous Polymer Intermediates

The porous polymer intermediates are formed by admixing a polymer and acompatible liquid, heating the mixture to a temperature which is usuallynear or above the softening temperature of the resin such thathomogeneous solution is formed, and then cooling the solution withoutsubjecting it to mixing or other shear forces to form a macroscopicallysolid homogeneous mass. When solid blocks of the intermediates are to beformed, the homogeneous solution is allowed to assume a desired shape bypouring it into an appropriate receptacle, which is usually made ofmetal or glass, and the solution allowed to cool under ambient roomconditions, unless otherwise noted. The rate of cooling under roomtemperature conditions will vary, depending on items such as samplethickness and composition, but will usually be in the range of fromabout 10° to about 20° C. per minute. The receptacle is typicallycylindrical in shape with a diameter of from about 0.75 to about 2.5inches and the solution is typically poured to a depth of from about0.25 to about 2.0 inches. When films of the intermediates are formed,the homogeneous solution is poured onto a metal plate which is heated toa temperature sufficient to allow the drawing of the solution into athin film. The metal plate is then placed into contact with a dry icebath to rapidly cool the film below its solidification temperature.

B. Porous Polymer

The microporous polymer is formed by extracting the compatible liquidused to form the porous polymer intermediate, typically by repetitivelywashing the intermediates in a solvent such as isopropanol ormethylethyl ketone, then drying the sold microporous mass.

EXAMPLES

The following examples and tables illustrate some of the variouspolymer/compatible liquid combinations which are useful in forming theporous polymer intermediates of this invention and various prior art orcommercially available microporous products. Solid blocks of theintermediates were formed for all of the exemplified combinations and,when so indicated in a table, thin films of the intermediate were alsoformed, using the procedure described above. As indicated in thefollowing tables, many of the intermediate compositions were used toform the microporous polymers of this invention, by using a suitablesolvent to extract the compatible liquid from the intermediatecomposition, and subsequently removing said solvent, as by evaporation.

Many of the compatible liquids which are illustrated in the followingexamples are, as indicated in the tables, functional liquids which areuseful not only as compatible liquids but also as flame retardants, slipagents, and the like. Thus, the intermediate compositions which areformed with such functional liquids are useful as solid polymeradditives and the like, as well as intermediates in the formation ofporous polymers. The functional liquids which appear in the followingexamples are indicated to be such by the presence of one or more of thefollowing symbols under column "Type of Functional Liquid": AF(Antifogging Agent); AO (Antioxidant); AR (Animal Repellant); FA (FuelAdditive); FG (Fragrance); FR (Flame Retardant); IR (Insect Repellant);L (Lubricant); M (Medicinal); MR (Moth Repellant); OM (Odor MaskingAgent); P (Plasticizer); PA (Polishing Agent); PE (Pesticide); PF(Perfume); S (Slip Agent); SF (Surfactant), and ST (Stabilizer).

EXAMPLES 1 TO 27

Examples 1 through 27 in Table V illustrate the formation of homogeneousporous polymer intermediates, in the form of cylindrical blocks having aradius of about 1.25 inches and a depth of about 2 inches, from highdensity polyethylene ("HDPE") and the compatible liquids found to beuseful, using the standard preparation procedure. The high densitypolyethylene was supplied by Allied Chemical under the designationPlaskon AA 55-003, having a melt index of 0.3 g/10 minutes and a densityof 0.954 g/cc. Many of the exemplified intermediates were extracted toform porous polymers, as indicated in the Table.

The details of preparation and the type of functionally useful liquidnoted are set forth in Table V:

                  TABLE V                                                         ______________________________________                                        HDPE                                                                                                               Type of                                                           %           Functional                               Ex. No.                                                                              Liquid Type and Liquid                                                                          Liq.   °C.                                                                         Liquid                                   ______________________________________                                               Saturated Aliphatic Acids                                              1      decanoic acid*    75     230  --                                              Primary Saturated Alcohols                                             2      decyl alcohol*    75     220  PF                                       3      1-dodecanol*      75     220  --                                              Secondary Alcohols                                                     4      2-undecanol*      75     220  --                                       5      6-undeconal*      75     230  --                                              Aromatic Amines                                                        6      N,N diethylaniline*                                                                             75     230  --                                              Diesters                                                               7      dibutyl sebacate* 70     220  L, P                                     8      dihexyl sebacate* 70     220  L, P                                            Ethers                                                                 9      diphenyl ether    75     220  PF                                       10     benzyl ether*     70     220  PF                                              Halogenated                                                            11     hexabromobenzene  70     250  FR                                       12     hexabromobiphenyl 75     200  FR                                       13     hexabromocyclodecane                                                                            70     250  FR                                       14     hexachlorocyclopentadiene                                                                       70     200  FR                                       15     octabromobiphenyl 70     280  FR                                              Terminally Double Bonded                                                      Hydrocarbons                                                           16     1-hexadecene*     75     220  --                                              Aromatic Hydrocarbons                                                  17     diphenylmethane*  75     220  OM                                       18     naphthalene*      70     230  MR                                              Aromatic Ketones                                                       19     acetophenone      75     200  PF                                              Aromatic Esters                                                        20     butyl benzoate*   75     220  L, P                                            Miscellaneous                                                          21     N,N--bis(2-hydroxyethyl)                                                                        70     250  --                                              tallowamine.sup.(1)*                                                   22     dodecylamine*     75     220  --                                       23     N--hydrogenated tallow-                                                                         50     240  SF                                              diethanol amine                                                        24     Firemaster BP-6.sup.(2)                                                                         75     200  --                                       25     Phosclere P315C*.sup.(3)                                                                        75     220  ST                                       26     Quinoline         70     240  M                                        27     dicocoamine.sup.(4)                                                                             75     220  --                                       ______________________________________                                         *The liquid was extracted from the                                            .sup.(1) A permanent internal antistatic agent having the following           properties was used: Boiling Point 1 mm Hg, °C., 215-220; Specific     Gravity 90° F., 0.896; Viscosity, SSU, 90° F.,                  .sup.(2) Michigan Chemical Corporation's trademark for its                    hexabromobiphenyl, a flame retardant having the following properties was      used: Softening Point, °C., 72; Density, 25° C., g/ml, 2.57     Viscosity, cps, 260-360 (Brookfield #3 spindle at 110° C.).       

                  TABLE VI                                                        ______________________________________                                        LDPE                                                                                                             Type of                                                         %             Functional                                 Liquid Type and Liquid                                                                             Liq.   °C.                                                                           Liquid                                     ______________________________________                                        Ex.                                                                           No..sup.(1)                                                                          Aliphatic Saturated Acids                                              28     caprylic acid*    70     210  --                                       29     decanoic acid*    70     190  --                                       30     hexanoic acid*    70     190  --                                       31     lauric acid*      70     220  --                                       32     myristic acid*    70     189  --                                       33     palmitic acid*    70     186  --                                       34     stearic acid*     70     222  --                                       35     undecanoic acid*  70     203  --                                              Unsaturated Aliphatic Acids                                            36     erucic acid.sup.(2) *                                                                           70     219  --                                       37     oleic acid*       70     214  PA                                              Aromatic Acids                                                         38     phenyl stearic acid*                                                                            70     214  --                                       39     xylyl behenic acid*                                                                             70     180  --                                        *The liquid was extracted from the                                            .sup.(1) Union Carbide Company's Bakelite"  polyethylene having the           following properties was used: Density, g/cm.sup.3, 0.922; Melt Index,        g/10 min., 21.                                                                .sup.(2) This is an acid with a density of 0.8602 g/cc and a melting poin     of 33-34° C..                                                     

    Ex. No.                                                                              Miscellaneous Acids                                                    40     Acintol FA2 (Tall Oil                                                         Acids).sup.(1) *  70     204  --                                       41     olefin acid L-6*  70     206  --                                       42     olefin acid L-9*  70     186  --                                       43     olefin acid L-11* 70     203  --                                       44     Rosin acid*       70     262  --                                       45     tolylstearic acid 70     183  --                                              Primary Saturated Alcohols                                             46     cetyl alcohol*    70     176  --                                       47     decyl alcohol*    70     220  PF                                       48     1-dodecanol*      75     200  --                                       49     1-heptadecanol*   70     168  --                                       50     nonyl alcohol*    70     174  PF                                       51     1-octanol*        70     178  --                                       52     oleyl alcohol*    70     206  FA                                       53     tridecyl alcohol  70     240  --                                       54     1-undecanol*      70     184  --                                       55     undecylenyl alcohol*                                                                            70     199  --                                              Secondary Alcohols                                                     56     dinonyl carbinol* 70     201  PF                                       57     diundecyl carbinol                                                                              70     226  --                                       58     2-octanol         70     174  --                                       59     2-undecanol*      70     205  --                                        *The liquid was extracted from the                                            .sup.(1) Arizona Chemical Company's trademark for a mixture of fatty          acids. The composition and physical properties are: Fatty Acid Compositio     (98.2% of total); Linoleic, Nonconjugated, %, 6: Oleic, %, 47; Saturated,     %, 3: Other fatty acids, %, 8: Specific Gravity, 25/25° C., 0.898;     Viscosity, SSU, 100° F., 94.                                      

           Aromatic Alcohols                                                      60     1-phenylethanol*  70     184  PF                                       61     1-phenyl-1-pentanol                                                                             70     196  --                                       62     phenyl stearyl alcohol*                                                                         70     206  --                                       63     nonyl phenol*     70     220  SF, PE                                          Cyclic Alcohols                                                        64     4- .sub.-t-butyl cyclohexanol*                                                                  70     190  PE                                       65     menthol*          70     206  PF                                              Other --OH                                                                    Containing Compounds                                                   66     Neodol-25.sup.(1) *                                                                             70     180  --                                       67     polyoxyethylene ether of                                                                        70     268  SF                                              oleyl alcohol.sup.(2)                                                  68     polypropylene glycol-                                                                           70     --   SF                                              425*.sup.(3)                                                                  Aldehydes                                                              69     salicylaldehyde*  70     188  PF                                        *The liquid was extracted from the                                            .sup.(1) Shell Chemical Company's trademark for its synthetic fatty           alcohol of 12-15 carbon atoms.                                                .sup.(2) Croda, Inc.' s, Volpo 3 surfactant having the following              properties was used: Acid Value, max., 2.0; Haze Pt., 1% aq. soln.,           insoluble; HLB value, calculated, 6.6; Iodine Value, Wijs, 57-62; pH of 3     aq. soln., 6-7; hydroxyl value,                                               .sup.(3) Union Carbide Company's trademark for its glycol having the          following properties; Apparent Specific Gravity, 20/20° C., 1.009;     Avg. hydroxyl number, mg. KOH/g, 265; Acid Number, mg KOH per g sample,       max., 0.2; pH at 25° C. in 10:6 isopropanol water soln.,          

     4.5-6.5.                                                                            Primary Amines                                                         70     dimethyldodecylamine                                                                            70     200  FA                                       71     hexadecylamine*   70     207  FA                                       72     octylamine*       70     172  FA                                       73     tetradecylamine*  70     186  FA                                              Secondary Amines                                                       74     bis(1-ethyl-3-methyl                                                                            70     190  --                                              pentyl) amine*                                                                Tertiary Amines                                                        75     N,N--dimethylsoya-                                                                              70     198  FA                                              amine*.sup.(1)                                                         76     N,N--dimethyltallow-                                                                            70     209  FA                                              amine*.sup.(2)                                                                Ethoxylated Amines                                                     77     N--stearyl diethanol                                                                            75     210  SF, AF                                          amine                                                                         Aromatic Amines                                                        78     aminodiphenylmethane                                                                            70     236  --                                       79     N-- --sec-butylaniline                                                                          70     196  --                                       80     N,N--diethylaniline*                                                                            70     --   --                                       81     N,N--dimethylaniline*                                                                           70     169  --                                       82     diphenylamine     70     186  AO, PE                                   83     dodecylaniline*   70     204  --                                       84     phenylstearyl amine*                                                                            70     205  --                                       85     N--ethyl-o-toluidine*                                                                           70     182  --                                       86     p-toluidine*      70     184  --                                        *The liquid was extracted from the                                            .sup.(1) A tertiary amine having the following properties was used: Cloud     point, °F., ASTM 100; Specific Gravity, 25/4°  C., 0.813;       Viscosity, SSU, at 25° C.,                                             .sup.(2) A tertiary amine having the following properties was used:           Melting Range, °F., 28 to 41: Cloud Point, °F., 60; Specifi     Gravity, 25/4° C., 0.803; Viscosity, SSU, 25° C.,          

     47.   Diamines                                                               87     1,8-diamino-p-menthane                                                                          70     188  --                                       88     N--erucyl-1,3-propane*                                                                          70     220  --                                              diamine                                                                       Miscellaneous Amines                                                          branched tetramine L-PS.sup.(1)*                                                                70     242  --                                       90     cyclododecylamine*                                                                              70     159  --                                              Amides                                                                 91     cocoamide*.sup.(2)                                                                              70     245  --                                       92     N,N--diethyltoluamide                                                                           70     262  IR                                       93     erucamide*.sup.(3)                                                                              70     250  L, P                                     94     hydrogenated tallow-                                                                            70     250  L, P                                            amide*                                                                 95     octadecylamide.sup.(4)                                                                          70     260  L, P                                     96     N--trimethylolpropane                                                                           70     255  L, P                                            stearamide                                                                    Aliphatic Saturated Esters                                             97     ethyl laurate*    70     175  --                                       98     ethyl palmitate*  70     171  --                                       99     isobutyl stearate*                                                                              70     194  L                                        100    isopropyl myristate*                                                                            70     192  --                                       101    isopropyl palmitate*                                                                            70     285  --                                       102    methyl caprylate  70     182  --                                       103    methyl stearate*  70     195  --                                       104    tridecyl stearate 70     202  L                                         *The liquid was extracted from the                                            .sup.(1) N--phenylstearol, 5, 9, 13                                           .sup.(2) An aliphatic amide having the following properties was used:         Appearance, Flake.; Flash Point, °C., Approx., 174; Fire Point,        °C., Approx., 185.                                                     .sup.(3) An amide having the following properties was used: Specific          Gravity, .88; Melting Pt., °C., 99-109; Flash Pt., °C.,         .sup.(4) Octadecylamide having the following properties was used:             Appearance, Flake; Flash Point, °C., Approx., 225; Fire Point,         °C. Approx., 250.                                                 

           Aliphatic Unsaturated Esters                                           105    butyloleate*      70     196  L                                        106    butylundecylenate*                                                                              70     205  --                                       107    stearylacrylate*  70     205  --                                              Alkoxy Esters                                                          108    butoxyethyl oleate*                                                                             70     200  --                                       109    butoxyethyl stearate*                                                                           70     205  --                                              Aromatic Esters                                                        110    benzylacetate     70     198  --                                       111    benzylbenzoate*   70     242  L, P                                     112    butylbenzoate*    70     178  L, P                                     113    ethylbenzoate*    70     200  L, P                                     114    isobutylphenylstearate*                                                                         70     178  L, P                                     115    methylbenzoate*   70     170  L, P                                     116    methylsalicylate* 70     200  L, P, PF                                 117    phenyllaurate*    70     205  L, P                                     118    phenylsalicylate  70     211  L, P, M, F                               119    tridecylphenylstearate*                                                                         70     215  L, P                                     120    vinylphenylstearate*                                                                            70     225  L, P                                            Diesters                                                               121    dibutylphthalate* 70     290  L, P                                     122    dibutyl sebacate* 70     238  L, P                                     123    dicapryl adipate  70     204  L, P                                     124    dicapryl phthalate                                                                              70     204  --                                       125    dicapryl sebacate 70     206  L, P                                     126    diethylphthalate* 70     280  IR                                       127    dihexylsebacate   70     226  --                                       128    dimethylphenylene 70     208  --                                              distearate*                                                            129    dioctyl maleate   70     220  --                                       130    di-iso-octyl phthalate                                                                          70     212  --                                       131    di-iso-octyl sebacate                                                                           70     238  --                                              Esters-Polyethylene Glycol                                             132    PEG 400 diphenylstearate                                                                        70     326  --                                              Polyhydroxylic Esters                                                  133    castor oil        70     270  --                                       134    glycerol dioleate*.sup.(1)                                                                      70     230  AF                                       135    glycerol distearate*.sup.(2)                                                                    70     201  AF                                       136    glycerol monooleate*.sup.(3)                                                                    70     232  AF                                       137    glycerol monophenyl-                                                                            70     268  --                                              stearate                                                               138    glycerol monostearate*.sup.(4)                                                                  70     211  AF                                       139    trimethylolpropane                                                                              70     260  --                                              monophenylstearate                                                            Ethers                                                                 140    dibenzylether*    70     189  PF                                       141    diphenylether*    75     200  --                                        *The liquid was extracted from the                                            .sup.(1) A glycerol ester having the following properties was used; Flash     Point, COC, °F., 520; Freezing Point, °C., 0; Viscosity at      25° C., cp, 90; Specific Gravity 25/20° C.,                     .sup.(2) A solid with a melting point of 29.1°                         .sup.(3) A glycerol ester having the following properties was used:           Specific Gravity, 0.94-0.953; Flash Point, COC, °F., 435; Freezing     Point, °C., 20; Viscosity at 25° C., cp,                        .sup.(4) A glycerol ester having the following properties was used: Form      at 25° C., Flakes; Flash Point, COC, °F., 410; Melting          Point, °C., 56.5-58.5.                                            

           Halogenated Ethers                                                     142    4-bromodiphenylether*                                                                           70     180  FR                                       143    FR 300 BA.sup.(1) 70     314  FR                                       144    hexachlorocyclopen-                                                                             70     196  PE, FR                                          tadiene*                                                               145    octabromobiphenyl*                                                                              70     290  FR                                              Terminal Double                                                               Bond Hydrocarbon                                                       146    1-nonene*         70     174  L                                               Internal Double                                                               Bond Hydrocarbon                                                       147    3-eicosene*       70     204  --                                       148    2-heptadecene*    70     222  --                                       149    2-nonadecene*     70     214  --                                       150    9-nonadecene*     70     199  --                                       151    2-nonene*         70     144  L                                        152    2-undecene        70     196  --                                              Aromatic Hydrocarbons                                                  153    diphenylmethane   75     200  PF                                       154                                                                                   ##STR1##         70     218  --                                       155    triphenylmethane  70     225  --                                              Aliphatic Ketones                                                      156    dinonylketone*    70     206  --                                       157    distearylketone*  70     238  --                                       158    2-heptadecanone   70     205  --                                       159    8-heptadecanone*  70     183  --                                       160    2-heptanone*      70     152  --                                       161    methylheptadecyl  70     225  --                                              ketone*                                                                162    methylnonyl ketone*                                                                             70     170  AR                                        *The liquid was extracted from the                                            .sup.(1) Dow Chemical Company's trademark for its decabromodiphenyl oxide     fire retardant having the following properties was used: Bromine, %,          81-83; Melting Point, min. 285° C.; Decomposition Temp., DTA,          425° C.                                                           

           Aliphatic Ketones                                                      163    methylpentadecyl  70     210  AR                                              ketone*                                                                164    methylundecyl ketone                                                                            70     205  --                                       165    2-nonadecanone    70     214  --                                       166    10-nonadecanone   70     194  --                                       167    8-pentadecanone*  70     178  --                                       168    11-pentadecanone* 70     262  --                                       169    2-tridecanone*    70     168  --                                       170    6-tridecanone*    70     205  --                                       171    6-undecanone*     70     188  --                                              Aromatic Ketones                                                       172    acetophenone*     70     190  PF                                       173    benzophenone      70     245  PF                                              Miscellaneous Ketones                                                  174    9-xanthone*       70     220  PE                                              Phosphorous Compounds                                                  175    trixylenyl phosphate*                                                                           70     304  FR                                              Miscellaneous                                                          176    N,N--bis(2-hydroxyethyl)                                                                        70     210  --                                              tallowamine*                                                           177    bath oil fragrance                                                                              70     183  FG                                              #5864K                                                                 178    EC-53 Styrenated nonyl                                                                          70     191  AO                                              phenol.sup.(1) *                                                       179    Mineral oil       50     200  L                                        180    Muget hyacinth    70     178  FG                                       181    Phosclere P315C*  70     200  --                                        *The liquid was extracted from the                                            .sup.(1) Akzo Chemie Nv.'s trademark for its styrenated hindered         

     phenol.                                                                             Miscellaneous                                                          182    Phosclere P576.sup.(1) *                                                                        70     210  AO                                       183    Quinalidine       70     173  --                                       184    Quinoline*        70     230  --                                       185    Terpineol Prime No. 1                                                                           70     194  M, PF                                    186    Firemaster BP-6   75     200  FR                                       187    benzylalcohol/1-  70     204  --                                              heptadecanol (50/50)*                                                  188    benzylalcohol/1-  70     194  --                                              heptadecanol (75/25)*                                                  ______________________________________                                         *The liquid was extracted from the                                            .sup.(1) Akzo Chemie Nv.'s styrenated hindered phenol.                   

Photomicrographs of the porous polymers of Examples 38 and 122 areillustrated in FIGS. 28 and 29, respectively. The photomicrographs, at2000X amplification, show the cellular structure with a significantamount of "foliage" uniformly present throughout the samples.

EXAMPLES 189 TO 193

Examples 190 through 194 in Table VII illustrate the formation ofhomogeneous porous polymer intermediates, by pouring the solution into aglass dish to form cylindrical blocks having a radius of about 1.75inches and a depth of about 0.25 inch, except where indicated, from"Noryl" polymer and the compatible liquids found to be useful, using thestandard preparation procedure. In the indicated instances, themicroporous polymer was likewise prepared.

The details of preparation and the type of functionally useful liquidnoted are set forth in Table VII:

                  TABLE VII                                                       ______________________________________                                                                             Type of                                                           %           Functional                               Ex. No. (1)                                                                           Liquid Type and Liquid                                                                         Liq.   °C.                                                                         Liquid                                   ______________________________________                                                Aromatic Amine                                                        189     diphenylamine    75     195  PE,A0                                            Diester                                                               190     dibutylphthalate 75     210  L                                                Halogenated Hydrocarbon                                               191     hexabromobiphenyl (2)                                                                          70     315  FR                                               Miscellaneous                                                         192     N,N--bis(2-hydroxyethyl)                                                                       75     250  --                                               tallowamine*                                                          193     N,N--bis(2-hydroxyethyl)                                                                       90     300  --                                               tallowamine                                                           ______________________________________                                         (1) General Electric Company's "Noryl", a blend of polyphenylene oxide        condensation polymer with polystyrene, having the following properties wa     used: Specific Gravity, 73° F., 1.06; Tensile Strength, psi. at        73° F., 9,600: Elongation at break, % at 73° F., 60; Tensil     Modulus, psi. at 73° F., 355,000; nad Rockwell Hardness, R119.         (2) The "Noryl" microporous polymers formed with hexabromo biphenyl and       N,N--bis(2hydroxyethyl) tallowamine were poured to depths of 0.5 inch.   

A photomicrograph of the microporous polymer of Example 192 isillustrated in FIG. 25. The photomicrograph, at 2500X amplification,shows the microcellular structure with spherical resin deposits on thewalls of the cells.

EXAMPLES 194 TO 236

Examples 194 through 236 in Table VIII illustrate the formation ofhomogeneous porous polymer intermediates, in the form of cylindricalblocks having a radius of about 1.25 inches and a depth of about 0.5inch, from polypropylene ("PP") and the compatible liquids found to beuseful, using the standard preparation procedure. In addition, in theindicated examples, blocks of about 6 inches in depth and/or thin filmswere made. Also, as indicated, the microporous polymer was prepared.

The details of preparation and the type of functionally useful liquidnoted are set forth in Table VIII:

                  TABLE VIII                                                      ______________________________________                                        PP                                                                                                            Type of                                                         %             Functional                                                                            Thin                                  Liquid Type and Liquid                                                                          Liq.   °C.                                                                           Liquid  Film                                  ______________________________________                                        Ex.  Unsaturated Acid                                                         No.                                                                           (1)                                                                           194  10-undecenoic acid*                                                                            70     260  M                                                Alcohols                                                                 195  2-benzylamino-1- 70     260  --                                               propanol                                                                 196  Ionol CP*        70     160  AO                                          197  3-phenyl-l-propanol                                                                            75     230  --                                          198  salicylaldehyde  70     185  PF                                               Amides                                                                   199  N,N--diethyl-m-toluamide                                                                       75     240  IR                                               Amines                                                                   200  aminodiphenylmethane*                                                                          70     230  --                                          201  benzylamine*     70     160  --                                          202  N--butylaniline  75     200  --                                          203  1,12-diaminododecane*                                                                          70     180  --                                          204  1,8-diaminooctane                                                                              70     180  --                                          205  dibenzylamine*   75     200  --                                          206  N,N--diethanolhexyl-                                                                           75     260  --                                               amine*                                                                   207  N,N--diethanoloctyl-                                                                           75     250  --                                               amine*                                                                   208  N,N--bis-β-hydroxyethyl                                                                   75     280  --                                               cyclohexylamine                                                          209  N,N--bis-(2-hydroxyethyl)                                                                      75     260  --                                               hexylamine                                                               210  N,N--bis-(2-hydroxyethyl)                                                                      75     260  --                                               octylamine                                                               ______________________________________                                         (1) Phillips Petroleum Company's "Marlex" polypropylene having the            following properties was used: Density, g/cm.sup.3, 0.908; Melt Flow, g/1     min. Melting Point, °F., 340; Tensile Strength at yield, psi,          2"/min., 5000; Hardness Shore D, 73.                                         Ex.  Esters                                                                   No.                                                                           211  benzylacetate*   75     200  --      --                                  212  benzylbenzoate*  75     235  L, P, PF                                                                              --                                  213  butylbenzoate    75     190  L, P    --                                  214  dibutylphthalate*                                                                              75     230  L, P    yes                                 215  methylbenzoate   70     190  L, P, PF                                                                              --                                  216  methylsalicylate*                                                                              75     215  L, P, PF                                                                              --                                  217  phenylsalicylate*                                                                              70     240  P       --                                       Ethers                                                                   218  dibenzylether    75     210  PF      --                                  219  diphenylether*   75     200  PF      yes                                      Halocarbons                                                              220  4-bromodiphenylether*                                                                          70     200  FR      --                                  221  1,1,2,2          70     180  FR      --                                       tetrabromoethane*                                                        222  1,1,2,2          90     180  FR      --                                       tetrabromoethane*                                                             Ketones                                                                  223  benzylacetone    70     200  --      --                                  224  methylnonylketone                                                                              75     180  --      --                                       Miscellaneous                                                            225  N,N--bis(2-hydroxethyl)                                                                        75     200  --      yes                                      tallowamine*                                                                  (1) & (2)                                                                226  N,N--bis(2-hydroxyethyl)                                                                       75     180  --      --                                       cocoamine (2)                                                            227  butylated hydroxy                                                                              70     160  AO      --                                       toluene                                                                  ______________________________________                                         (1) A block of about 6 inches in depth was also prepared                      (2) A permanent internal antistatic agent, having the following physical      properties was used: Boiling Point, 1 mm Hg, °C., 170; Viscosity,      SSU, 90° F., 367.                                                     Ex.  Miscellaneous (cont'd.)                                                  No.                                                                           228  D.C. 550 Silicone                                                                              50     260  S, L    --                                       Fluid (1)                                                                229  D.C. 556 Silicone                                                                              70     190  S, L    --                                       Fluid*                                                                   230  EC-53            75     210  --      --                                  231  N--hydrogenated rape-                                                                          75     210  SF      --                                       seed diethanol                                                                amine*                                                                   232  N--hydrogenated tallow                                                                         75     225  SF      --                                       diethanol amine                                                          233  Firemaster BP-6  75     200  FR      --                                  234  NBC oil          75     190  --      --                                  235  Quinaldine*      70     200  --      --                                  236  Quinoline*       75     220  M       --                                  ______________________________________                                         *The liquid was extracted from the solid.                                     (1) Dow Corning's trademark for its phenylmethyl polysiloxane having the      following properties was used: Viscosity 115CS and serviceable from -40 t     450° F. in open systems, and to 600° F. in closed systems. 

Photomicrographs of the porous polymer of Example 225 are illustrated inFIGS. 2 through 5. The photomicrographs of FIGS. 2 and 3, at 55X and550X amplification, respectively, show the macro structure of themicroporous polymer. The photomicrographs of FIGS. 4 and 5, at 2,200Xand 5,500X amplification, respectively, show the microcellular structureof the polymer as well as the interconnecting pores.

EXAMPLES 237 TO 243

Examples 237 through 243 in Table IX illustrate the formation ofhomogeneous porous polymer intermediates, in the form of cylindricalblocks having a radius of about 1.25 inches and a depth of about 0.5inch, from polyvinylchloride ("PVC") and the compatible liquids found tobe useful, using the standard preparation procedure. Many of theexemplified intermediates were extracted to form porous polymers, asindicated in the Table.

The details of preparation and the type of functionally useful liquidnoted are set forth in Table IX:

                  TABLE IX                                                        ______________________________________                                        PVC                                                                                                                Type of                                                          %            Functional                               Ex. No. (1)                                                                           Liquid Type and Liquid                                                                        Lig.   °C.                                                                          Liquid                                   ______________________________________                                                Aromatic Alcohols                                                     237     4-methoxybenzyl-                                                                              70     150   PF                                               alcohol*                                                                      Other - (OH)                                                                  Containing Compounds                                                  238     1-3,-dichloro-2-pro-                                                                          70     170   --                                               panol*                                                                239     menthol*        70     180   PF                                       240     10-undecene-1-ol*                                                                             70     204-                                                                          210   --                                               Halogenated                                                           241     Firemaster T33P* (2)                                                                          70     165   FR                                       242     Firemaster T13P* (3)                                                                          70     175   FR                                               Aromatic Hydrocarbons                                                 243     trans-stilbene* 70     190   --                                       ______________________________________                                         *The liquid was extracted from the solid.                                     (1) The polyvinylchloride used was of dispersion grade made by American       Hoechst, having an inherent viscosity of 1.20, a density of 1.40 and bulk     density of 20.25 pounds per cubic foot.                                       (2) Michigan Chemical Corporation's trademark for its tris                    (1,3dichloroisopropyl) phosphate fire retardant having the following          properties: Chlorine content, theoretical, %, 49.1; Phosphorous content,      theoretical, %, 7.2; Boiling Point, 4 mm Hg, abs. °C., 200             (decomposes at 200° C.); Refractive Index, 1.50.9; Viscosity,          Brookfield, 73° F., Centipoises, 2120.                                 Structure: [ (ClCH.sub.2).sub.2 CHO].sub.3 P-O                                (3) Michigan Chemical Corporation's trademark for its trishalogenated         propylphosphate flame retardant having the following properties: Specific     Gravity, at 25° C./25° C., 1.88; Viscosity, at 25°       C., centistokes, 1928; Refractive Index, 1.540; pH, 6.4; Chlorine, %,         18.9; Bromine, %, 42.5; Phosphorous, %, 5.5.                             

A photomicrograph of the porous polymer of Example 242 is illustrated inFIG. 27. The photomicrograph, at 2000X amplification, shows theextremely small cell size of this microporous polymer in contrast to thecell structure exemplified by FIGS. 7, 13, 18, 20, and 24, wherein thecell size is larger and more readily observable at a comparablemagnification. The photomicrograph also shows the presence of a largeamount of resin masking the basic cell structure.

EXAMPLES 244 TO 255

Examples 244 through 255 in Table X illustrate the formation ofhomogeneous porous polymer intermediates, in the form of cylindricalblocks having a radius of about 1.25 inches and a depth of about 2.0inches, from methylpentene ("MPP") polymer and the compatible liquidsfound to be useful, using the standard preparation procedure. Many ofthe exemplified intermediates were extracted to form porous polymers, asindicated in the Table.

The details of preparation and the type of functionally useful liquidnoted are set forth in Table X:

                  TABLE X                                                         ______________________________________                                        MPP                                                                                                              Type of                                                                       Functional                                 Liquid Type and Liquid                                                                            % Liq.  °C.                                                                           Liquid                                     ______________________________________                                        Ex. No. (1)                                                                           Saturated Aliphatic Acid                                              244     decanoic acid*  75      230  --                                               Saturated Alcohols                                                    245     1-dodecanol*    75      230  --                                       246     2-undecanol*    75      230  --                                       247     6-undecanol*    75      230  --                                               Amine                                                                 248     dodecylamine    75      230  FA                                               Esters                                                                249     butylbenzoate*  75      210  L, P, PF                                 250     dihexylsebacate*                                                                              70      220  L, P                                             Ethers                                                                251     dibenzylether*  70      230  PF                                       Ex. No. Hydrocarbons                                                          252     1-hexadecene*   75      220  --                                       253     naphthalene*    70      240  MR                                               Miscellaneous                                                         254     EC-53*          75      230  AO                                       255     Phosclere P315C*                                                                              75      250  --                                       ______________________________________                                         *The liquid was extracted from the solid.                                     (1) Mitsui's methylpentene polymer having the following properties was        used: Density, g.cc, 0.835; Melting Point °C., 235; Tensile            Strength at Break, kg/cm.sup.2, 230; Elongation at Break %, 30, Rockwell      Hardness, R, 85.                                                         

A photomicrograph of the porous polymer of Example 253 is illustrated inFIG. 22. The photomicrograph, at 2400X amplification, shows theextremely flattened cell walls, as comparable to the configurationobserved in FIG. 14.

EXAMPLES 256 TO 266

Examples 256 through 266 in Table XI illustrate the formation ofhomogeneous porous polymer intermediates, in the form of cylindricalblocks having a radius of about 1.25 inches and a depth of about 0.5inch, from polystyrene ("PS") and the compatible liquids found to beuseful, using the standard preparation procedure. All of the exemplifiedintermediates were extracted to form porous polymers.

The details of preparation and the type of functionally useful liquidnoted are set forth in Table XI.

                  TABLE XI                                                        ______________________________________                                                                             Type of                                                           %           Functional                               Ex. No.(1)                                                                            Liquid Type and Liquid                                                                         Liq.   °C.                                                                         Liquid                                   ______________________________________                                        256     Firemaster T-13P 70     250  FR                                       257     hexabromobiphenyl                                                                              70     260  FR                                       258     Phosclere P315C  70     270  --                                       259     Phosclere P576   70     285  AO                                       260     tribromoneopentylalcohol                                                                       70     210  FR                                       261     FR 2249 (2)      70     240  FR                                       262     Fyrol CEF (3)    70     250  FR                                       263     Firemaster T33P (4)                                                                            70     210  FR                                       264     Fyrol FR 2 (5)   70     240  FR                                       265     dichlorobenzene  80     160  MR, FR                                   266     1-dodecanol      75     --   --                                       ______________________________________                                         (1) Monsanto Chemical Company's "Lustrex" polystyrene having the followin     physical properties was used: Impact Strength, ft. lbs./in notch (Inj.        molded), 0.40; Tensile Strength, psi, 7500; Elongation, %, 2.5; Elastic       Modulus, psi, XID.sup.5, 4.5; Deflection Temp., under load 264, psi,          °F., 200; Specific Gravity, 1.05; Rockwell Hardness, M75; Melt         Flow, g/10 min., 4.5.                                                         (2) Dow Chemical Corporation's trademark for its fire retardant having        composition and properties: Tribromoneopentyl alcohol, 60%, Voranol CP.       3000 polyol, 40%; Bromine, %, 43; hydroxyl No. 130; Viscosity, cps,           25° C. (approx.) 1600; Density, gm/cc, 1.45.                           (3) Stauffer Chemical Company's trademark for its tris chloroethyl            phosphate fire retardant having the following properties; Boiling Point,      at 0.5 mm Hg abs., °C., 145, at 760 mm hg abs., °C.,            decomposes; Chlorine content, wt. %, 36.7; Phosphorous content, wt. %,        10.8; Refractive Index at 20° C., 1.4745; Viscosity, cps at            73° F. (22.8° C.), 40.                                          (4) Michigan Chemical Corporation's trademark for its                         tris(1,3dichloroisopropyl phosphate) fire retardant having the following      properties; Chlorine content, theoretical, %, 49.1; Phosphorous content,      theoretical, &, 7.2; Boiling Point, 4 mm Hg abs., °C./ 200             (decomposes at 200° C.); Refractive Index, 1.5019; Viscosity,          Brookfield, 73° F., Centipoises, 2120.                                 Structure: [ (ClCH.sub.2).sub.2 CHO].sub.3 P-O                                (5) Stauffer Chemical Company's trademark for its tris (dichloropropyl)       phosphate flame retardant additive having the following properties:           Melting Point, °F., Approx., 80; Refractive Index n.sub.d at           25° C., 1.5019; Viscosity, Brookfield at 22.8° C., cps,         2120.                                                                    

A photomicrograph of the microporous polymer of Example 260 isillustrated in FIG. 26. Although the cells are small compared to thecells illustrated in FIGS. 4, 7, 13, 18, and 25, the basic microcellularstructure is present.

EXAMPLE 267

This Example illustrates the formation of a homogeneous porous polymerintermediate from 30% high impact polystyrene (1) and 70%hexabromobiphenyl, using the standard preparation procedure and heatingthe mixture to 280° C. The polymer intermediate thus formed was about2.5 inches in diameter and about 0.5 inch in depth. Thehexabromobiphenyl is useful as a flame retardant and the porousintermediate is useful as a solid flame retardant additive.

EXAMPLE 268

This Example illustrates the formation of a homogeneous porous polymerintermediate from 25% acrylonitrile-butadiene-styrene terpolymer (2) and75% diphenylamine, using the standard preparation procedure and heatingthe mixture to 220° C. The polymer intermediate thus formed was about2.5 inches in diameter and about 2 inches in depth. The microporouspolymer was formed by extracting the diphenylamine. The diphenylamine isuseful as a pesticide and antioxidant and the porous polymerintermediate has the same utility.

EXAMPLES 269 AND 270

The homogeneous porous polymer intermediates were formed from 25%chlorinated polyethylene thermoplastic supplied by Dow, having a meltviscosity of 15 poise, 8 percent crystallinity, and containing 36percent chlorine and 75% N,N-bis(2-hydroxyethyl)tallowamine (Example270) and 75% chlorinated polyethylene thermoplastic and 25% 1-dodecanol(Example 271), using the standard preparation procedure and heating to220° C. The porous polymer intermediates were about 2.5 inches indiameter and about 2 inches in depth.

EXAMPLE 271

The homogeneous porous polymer intermediate was formed using thestandard preparation procedure and heating to 210° C. from 25%chlorinated polyethylene elastomer, as used in Example 271 and 75%diphenylether. The porous polymer intermediates were about 2.5 inches indiameter and about 2 inches in depth. The diphenylether is useful as aperfume and the intermediate is also useful in perfumes.

EXAMPLES 272 TO 275

Examples 272 through 275 in Table XII illustrate the formation ofhomogeneous porous polymer intermediates, in the form of cylindricalblocks having a radius of about 1.25 inches and a depth of about 0.5inch from styrene-butadiene ("SBR") rubber (1) and the compatibleliquids found to be useful using the standard preparation procedure. Inaddition to the cylindrical blocks, as indicated, thin films were alsoformed.

The details of preparation and the type of functionally useful liquidnoted are set forth in Table XII:

                  TABLE XII                                                       ______________________________________                                        SBR                                                                                                              Type                                                                          of Func-                                   Ex.                   %            tional Thin                                No.  Liq. Type and Liquid                                                                           Liq.   °C.                                                                          Liquid Film                                ______________________________________                                        272  N,N--bis(2-hydroxyethyl)                                                                       80     195   --     yes                                      tallowamine                                                              273  decanol*         70     190   PF     yes                                 274  diphenylamine    70     200-  PE, AO yes                                                              210                                              275  diphenylether    70     195   PF     yes                                 ______________________________________                                         *The liquid was extracted from the solid.                                

EXAMPLES 276 TO 278

Examples 277 through 279 in Table XIII illustrate the formation ofhomogeneous porous polymer intermediates, in the form of cylindricalblocks having a radius of 1.25 inches and a depth of about 0.5 inch from"Surlyn" (1) and the compatible liquids found to be useful, using thestandard preparation procedure. In addition to the cylindrical blocks,as indicated, thin films were also formed. Two of the exemplifiedintermediates were extracted to form porous polymers, as indicated inthe Table.

The details of preparation and the type of functionally useful liquidnoted are set forth in Table XIII:

                  TABLE XIII                                                      ______________________________________                                        SURLYN                                                                                                          Type of                                     Ex.                   %           Functional                                                                            Thin                                No.(1) Liq. Type and Liquid                                                                         Liq.   °C.                                                                         Liquid  Film                                ______________________________________                                        276    N,N--bis(2-hydroxy-                                                                          70     190  --      yes                                        ethyl) tallowamine    195                                              277    diphenylether* 70     200  PF      yes                                 278    dibutylphthalate                                                                             70     195  L       yes                                 ______________________________________                                         *The liquid was extracted from the solid.                                

Photomicrographs of the porous polymer of Example 277 are illustrated inFIGS. 23 and 24. FIG. 23, at 255X amplification, shows themacrostructure of the polymer. FIG. 24, at 2550X amplification,illustrates the microcellular structure of the polymer with slight"foliage" and relatively thick cell walls, as compared with, forexample, FIG. 25.

EXAMPLE 279

The homogeneous porous polymer intermediate was formed, using thestandard preparation procedure and heating to 200° C., from a highdensity polyethylene-chlorinated polyethylene blend, equal parts, and75% 1-dodecanol. The porous polymer intermediate was cast in a filmhaving a thickness of about 20 to 25 mils. The HDPE and CPE wereutilized in previous Examples.

EXAMPLE 280

The homogeneous porous polymer intermediate was formed, using thestandard preparation procedure and heating to 200° C., from a highdensity polyethylene-polyvinylchloride blend, equal parts, and 75%1-dodecanol. The intermediate thus formed was about 2 inches in depthand about 2.5 inches in diameter. The HDPE and PVC were as utilized inprevious Examples.

EXAMPLE 281

The homogeneous porous polymer intermediate was formed, using thestandard preparation procedure and heating to 200° C., from a highdensity polyethylene/acrylonitrile-butadiene-styrene terpolymer blend,equal parts, and 75% 1-dodecanol. The intermediate thus formed was about2 inches in depth and about 2.5 inches in diameter. The HDPE and ABSwere as utilized in previous Examples.

EXAMPLES 282 TO 285

Examples 282 through 285 in Table XIV illustrate the formation ofhomogeneous porous polymer intermediates, in the form of cylindricalblocks having a radius of 1.25 inches and a depth of about 2 inches,from low density polyethylene/chlorinated polyethylene blend, equalparts, and the compatible liquids found to be useful, using the standardpreparation procedure. In Example 283, the aforementioned method wasemployed, but the intermediate was cast into a film having a thicknessof about 20 to 25 mils. The LDPE and CPE were as utilized in previousExamples.

The details of preparation and the type of functionally useful liquidnoted are set forth in Table XIV:

                  TABLE XIV                                                       ______________________________________                                                                             Type of                                                                       Functional                               Ex. No.                                                                              Liquid Type and Liquid                                                                         % Liq.  °C.                                                                         Liquid                                   ______________________________________                                        282    1-dodecanol      75      200  --                                       283    diphenylether    75      200  PF                                       284    diphenylether    50      200  PF                                       285    N,N--bis(2-hydroxyethyl)                                                                       75      200  --                                              tallowamine                                                            ______________________________________                                    

EXAMPLES 286 AND 287

The homogeneous porous polymer intermediates were formed from a lowdensity polyethylene/polypropylene blend, equal parts, and 75%,N,N-bis(2-hydroxyethyl)tallowamine (Example 286) and low densitypolyethylene/polypropylene blend, equal parts, and 50%N,N-bis(2-hydroxyethy)tallowamine (Example 287) using the standardpreparation procedure and heating to 220° C. for Example 286 and to 270°C. for Example 288. Both porous polymer intermediates were about 2.5inches in diameter and about 2 inches in depth. The LDPE and PP were asutilized in previous Examples.

EXAMPLE 288

The homogeneous porous polymer intermediate was formed, using thestandard preparation procedure and heating to 200° C., from 50%N,N-bis(2-hydroxyethyl)tallowamine and 50% polypropylene/polystyreneblend (25 parts polypropylene). The porous polymer intermediates wereabout 2.5 inches in diameter and about 2 inches in depth. The PP and PSwere as utilized in previous Examples.

EXAMPLE 289

The homogeneous porous polymer intermediate was formed, using thestandard preparation procedure and heating to 200° C., from 75%1-dodecanol and a polypropylene/chlorinated polyethylene blend, equalparts. The porous polymer intermediate was about 2.5 inches in diameterand about 0.5 inch in depth. The PP and CPE were as utilized in previusExamples.

EXAMPLES 290 TO 300

Examples 290 through 300 illustrate the polymer-compatible liquidconcentration range useful for the formation of a homogeneous porouspolymer intermediate from high density polyethylene andN,N-bis(2-hydroxyethyl)tallowamine. In each Example the intermediateswere about 2 inches in depth and about 2.5 inches in diameter. The HDPEwas as utilized in previous Examples.

The details of preparation and any physical characteristics noted areset forth in Table XV:

                  TABLE XV                                                        ______________________________________                                        Ex. No.                                                                              % Liq.   °C.                                                                              Remarks                                             ______________________________________                                        290    95       275       very weak; no solid integrity;                                                not operable                                        291    90       --        very greasy; liquid leaching                                                  out; upper liquid limit was                                                   exceeded                                            292    80       250       greasy                                              293    75       220       greasy                                              294    70       250       hard solid                                          295    65       220       --                                                  296    60       250       hard solid                                          297    55       220       --                                                  298    50       240-260   hard solid                                          299    40       260       hard solid                                          300    30       200       hard solid                                          ______________________________________                                    

A photomicrograph of the porous polymer of Example 300 is illustrated inFIG. 19, at 2000X amplification. The cells are not clearly visible atthis amplification. FIG. 19 can be compared to FIG. 17, at 2475Xamplification, wherein the cell sizes are also very small at a similarpolymer concentration of 70%.

EXAMPLES 301 TO 311

These Examples illustrate the polymer-compatible liquid concentrationrange useful for the formation of a homogeneous porous polymerintermediate from low density polyethylene andN,N-bis(2-hydroxyethyl)tallowamine. In each example the intermediate wasabout 0.5 inch in depth and about 2.5 inches in diameter. The LDPE wasas utilized in previous Examples.

The details of preparation and any physical characteristics noted areset forth in Table XVI:

                  TABLE XVI                                                       ______________________________________                                        Ex. No.                                                                              % Liq.   °C.                                                                              Remarks                                             ______________________________________                                        301    95       275       very weak, no solid integrity;                                                not operable                                        302    90       240       very greasy; liquid leaching                                                  out; upper liquid limit was                                                   exceeded                                            303    80       260       hard solid                                          304    75       210       hard solid                                          305    70       210       hard solid                                          306    66       200       hard solid                                          307    60       280       hard solid                                          308    50       280-290   hard solid                                          309    40       285       hard solid                                          310    30       285       hard solid                                          311    20       280-300   hard solid                                          ______________________________________                                    

Photomicrographs of the porous polymers of Examples 303, 307 and 310 areillustrated in FIGS. 14-15 (at 250X and 2500X amplification,respectively), 16 (at 2500X amplification), and 17 (at 2475Xamplification), respectively. The Figures show the decreasing cell size,from very large (FIG. 15, 20% polymer) to very small (FIG. 17, 70%polymer), with increasing polymer content. The relatively flattened cellwalls of the 20% polymer, Example 303, are similar to the methyl pentenepolymer (FIG. 22) and are observable in FIG. 14. FIG. 15 is anenlargement showing part of a cell wall illustrated in FIG. 14. Themicrocellular structure of the porous polymer is observable in FIG. 16.

EXAMPLES 312 TO 316

Examples 312 to 316 illustrate the polymer-compatible liquidconcentration range useful for the formation of a homogeneous porouspolymer intermediate from low density polyethylene and diphenylether. Ineach Example the intermediate was about 0.5 inch in depth and about 2.5inches in diameter. The LDPE was as utilized in previous Examples.

The details of preparation and any physical characteristics noted areset forth in Table XVII:

                  TABLE XVII                                                      ______________________________________                                        Ex. No.                                                                              % Liq.   °C.                                                                              Remarks                                             ______________________________________                                        312    90       185       very greasy; no solid integrity;                                              not operable                                        313    80       185       very greasy; near upper liquid                                                limit but still operable                            314    75       200       wet; strong                                         315    70       190-200   slightly greasy                                     316    60       200       hard solid                                          ______________________________________                                    

EXAMPLES 317 TO 322

Examples 317 to 321 illustrate the polymer-compatible liquidconcentration range useful for the formation of a homogeneous porouspolymer intermediate from low density polyethylene and 1-hexadecene. Ineach Example the intermediate was about 2 inches in depth and about 2.5inches in diameter. The LDPE was as utilized in previous Examples.

The details of preparation and any physical characteristics noted areset forth in Table XVIII:

                  TABLE XVIII                                                     ______________________________________                                        Ex. No.   % Liq.  °C.                                                                             Remarks                                            ______________________________________                                        317       90      180      good strength                                      318       80      180      little strength, operable                          319       75      200      little strength, operable                          320       70      177      --                                                 321       50      180      good strength                                      ______________________________________                                    

EXAMPLES 322 TO 334

These Examples illustrate the polymer-liquid concentration range usefulfor the formation of a homogeneous porous polymer intermediate frompolypropylene and N,N-bis(2-hydroxyethyl)tallowamine. In each Examplethe intermediate was about 0.5 inch in depth and 2.5 inches in diameter.In addition, as indicated, films were made. The PP was as utilized inprevious Examples.

The details of preparation and any physical characteristics noted areset forth in Table XIX:

                  TABLE XIX                                                       ______________________________________                                        Ex. No. % Liq.  °C.                                                                             Remarks    Thin Film                                 ______________________________________                                        322     90      200      quite wet  yes                                       323     85      200      --         --                                        324     80      200      strong     yes                                       325     75      180      dry and hard                                                                             yes                                       326     70      200      --         yes                                       327     65      210      --         --                                        328     60      210      --         yes                                       329     50      200      --         yes                                       330     40      210      --         yes                                       331     36.8    175      white-crystalline                                                                        --                                        332     25      180      --         --                                        333     20      180      --         yes                                       334     15      180      --         --                                        ______________________________________                                    

Photomicrographs of Examples 322, 326, 328, 330 and 333 are illustratedin FIGS. 6 through 10, respectively (at 1325X, 1550X, 1620X, 1450X, and1250X amplification, respectively). The extreme foliage of the 10%polymer microporous polymer is shown by FIG. 6, yet the microcellularstructure is still maintained. These Figures illustrate the decreasingcell size as the amount of polymer is increased. However, themicrocellular structure is present in each example despite the smallcell size.

EXAMPLES 335 TO 337

The Examples illustrate the polymer-compatible liquid concentrationrange useful for the formation of a homogeneous porous polymerintermediate from polypropylene and diphenylether. In each Example theintermediate was about 0.5 inch in depth and about 2.5 inches indiameter. In addition, as indicated, thin films were also made. The PPwas as utilized in previous Examples.

The details of preparation and any physical characteristics noted areset forth in Table XX:

                  TABLE XX                                                        ______________________________________                                        Ex. No.  % Liq.        °C.                                                                           Thin Film                                       ______________________________________                                        335      90            200    yes                                             336      80            200    yes                                             337      70            200    yes                                             ______________________________________                                    

Photomicrographs of the porous polymer of Examples 335, 336 and 337 areillustrated in FIGS. 11 (2000X amplification), 12 (2059X amplification)and 13 (1950X amplification). The FIGs. illustrate that as the polymerconcentration is increased, the pore size decreases, FIG. 11 illustratesthe smooth cell walls, while FIGS. 12 and 13 illustrate the cells andconnecting pores. In each of the Figures, the microcellular structure ispresent.

EXAMPLES 338 TO 346

These Examples illustrate the polymer-compatible liquid concentrationrange useful for the formation of a homogeneous porous polymerintermediate from styrene-butadiene rubber andN,N-bis(2-hydroxyethyl)tallowamine. In each Example the intermediate wasabout 0.5 inch in depth and 2.5 inches in diameter. In addition, asindicated, thin films were made. The SBR was as utilized in previousExamples.

The details of preparation and any physical characteristics noted areset forth in Table XXI:

                  TABLE XXI                                                       ______________________________________                                        Ex. No.                                                                              % Liq.  °C. Remarks    Thin Film                                ______________________________________                                        338    90      200        weak, beyond the                                                                         yes                                                                upper liquid limit                                  339    80      195        rubbery    yes                                      340    75      195        rubbery    yes                                      341    70      195        rubbery    yes                                      342    60      200        rubbery    yes                                      343    50      not reported                                                                             rubbery    yes                                      344    40      not reported                                                                             rubbery    yes                                      345    30      not reported                                                                             rubbery    yes                                      346    20      not reported                                                                             rubbery    yes                                      ______________________________________                                    

Photomicrographs for the styrene-butadiene rubber microporous polymer ofExamples 339 and 340 are illustrated in FIGS. 20 (2550X amplification)and 21 (2575X amplification). The Figures illustrate the microcellularstructure of the microporous polymers. FIG. 21 also shows the presenceof spherical polymer deposits on the cell walls.

EXAMPLES 347 TO 352

Examples 347 through 352 illustrate the polymer-compatible liquidconcentration range useful for the formation of a homogeneous porouspolymer intermediate from styrene-butadiene rubber and decanol. In eachExample the intermediate was about 0.5 inch in depth and 2.5 inches indiameter. In addition, as indicated, thin films were made. The SBR wasas utilized in previous examples.

The details of preparation and any physical characteristics noted areset forth in Table XXII:

                  TABLE XXIII                                                     ______________________________________                                        Ex. No.  % Liq.      °C. Remarks                                       ______________________________________                                        353      80          not reported                                                                             --                                            354      70          200-210    --                                            355      60          215        --                                            356      50          200-210    --                                            ______________________________________                                    

EXAMPLES 357 TO 361

Examples 357 through 361 illustrate the polymer-compatible liquidconcentration range useful for the formation of a homogeneous porouspolymer intermediate from a "Surlyn" resin as utilized in previousExamples and N,N-bis(hydroxyethyl)tallowamine. In each Example theintermediate was about 0.5 inch in depth and 2.5 inches in diameter. Inaddition, as indicated, thin films were made.

The details of preparation and any physical characteristics noted areset forth in Table XXIV:

                  TABLE XXIV                                                      ______________________________________                                        Ex. No.  % Liq.     °C. Thin Films                                     ______________________________________                                        357      70         190-195    yes                                            358      60         190        yes                                            359      50         not reported                                                                             yes                                            360      40         not reported                                                                             yes                                            361      30         not reported                                                                             yes                                            ______________________________________                                    

EXAMPLES 362 TO 370

These Examples illustrate the polymer-compatible liquid concentrationrange useful for the formation of a homogeneous porous polymerintermediate from a "Surlyn" resin as utilized in previous Examples anddiphenylether. In each Example the intermediate was about 0.5 inch indepth and about 2.5 inches in diameter. In addition, as indicated, thinfilms were made.

The details of preparation and any physical characteristics noted areset forth in Table XXV:

                  TABLE XXV                                                       ______________________________________                                        Ex. No.  % Liq.     °C. Thin Films                                     ______________________________________                                        362      90         207        yes                                            363      80         190        yes                                            364      70         200        yes                                            365      60         185        yes                                            366      50         not reported                                                                             yes                                            367      40         not reported                                                                             --                                             368      30         not reported                                                                             --                                             369      20         not reported                                                                             --                                             370      10         not reported                                                                             --                                             ______________________________________                                    

EXAMPLES 371 TO 379

Examples 371 through 379 illustrate the polymer-compatible liquidconcentration range useful for the formation of a homogeneous porouspolymer intermediate from a "Surlyn" resin as utilized in previousExamples and dibutylphthalate. In each Example the intermediate wasabout 0.5 inch in depth and about 2.5 inches in diameter.

The details of preparation and any physical characteristics noted areset forth in Table XXVI:

                  TABLE XXVI                                                      ______________________________________                                        Ex. No.  % Liq.      °C. Remarks                                       ______________________________________                                        371      90          220        --                                            372      80          208        --                                            373      70          195        --                                            374      60          200        --                                            375      50          200        --                                            376      40          not reported                                                                             --                                            377      30          not reported                                                                             --                                            378      20          not reported                                                                             --                                            379      10          not reported                                                                             --                                            ______________________________________                                    

PRIOR ART EXAMPLES 380-384 EXAMPLES 380 TO 384

Examples 380 to 384 are reproductions of various prior art compositionswhich are shown to have a physical structure different from that of thepresent invention.

EXAMPLE 380

A porous polymer was prepared in accordance with the process of Example1 of U.S. Pat. No. 3,378,507, as modified to obtain a product with somephysical integrity and to utilize a soap as the water-soluble anionicsurfactant, in place of sodium bis(2-ethylhexyl)sulfosuccinic.

In a Brabender-Plasti-Corder internally heated blender, 331/2 parts byweight of Exxon Chemical Corporation type LD 606 polyethylene and 662/3part of Ivory soap flakes were mixed at a machine temperature of about350° F., until a homogeneous blend was formed. The material was thencompression molded with a rubber type mold having a 2.5 inch by 5.0 inchcavity of a depth of 20 mils., at a temperature of about 350° F. and apressure of 36,000 pounds per square inch. The resulting sample wascontinuously washed for about three days in a slow flowing stream of tapwater and then sequentially washed by immersion in eight distilled waterbaths, each for a period of about one hour. The resulting sample stillretained some soap and had poor handling properties.

FIGS. 47 and 48 are photomicrographs of the product of Example 380, at195X and 2,000X amplification, respectively. It is apparent that theproduct is relatively non-uniform polymeric structure having neitherdistinct cellular cavities nor interconnecting pores.

EXAMPLE 381

A porous polymer was prepared in accordance with the process of Example2, sample D, of U.S. Pat. No. 3,378,507, as modified to obtain a samplehaving some handling strength.

In a Brabender-Plasti-Corder internally heated blender, 75 parts ofIvory soap flakes and 25 parts of Exxon Chemical Corporation type LD 606polyethylene were mixed at a machine temperature of about 350° F. and asample temperature of about 330° F. until a homogeneous blend wasformed. The material was then injection molded in a one-ounceWatson-Stillman injection molding machine having a mold cavity diameterof two inches and a depth of 20 mils. The resulting sample wascontinuously washed for about three days in a slowly flowing stream oftap water and then sequentially washed by immersion in eight distilledwater baths, each for a period of about one hour. The resulting samplestill retained some soap.

FIGS. 45 and 46 are photomicrographs of the product of Example 381, at240X and 2400X amplification, respectively. The product of this exampledoes not have the typical cellular structure of the present invention,as is apparent from the photomicrographs.

EXAMPLE 382

In accordance with the process of Example 3, sample A, of U.S. Pat. No.3,378,507, a porous polymer was prepared.

In a Brabender-Plasti-Corder internally heated blender, 25 parts ofNovamont Corporation type F300 8N19 polypropylene and 75 parts of Ivorysoap flakes were mixed at a machine temperature of about 330° F. until ahomogeneous blend was formed. The material was then compression moldedwith a rubber type mold. The resulting sample was found to have verylittle strength. A portion of the resulting sample was continuouslywashed for about three days in a slowly flowing stream of tap water andthen sequentially washed by immersion in eight distilled water baths,each for a period of about one hour. The washed product was found tohave extremely poor handling characteristics.

FIGS. 51 and 52 are photomicrographs of the product of Example 382 at206X and 2000X amplification, respectively. The photomicrographs showthat the product does not have the cellular structure of the presentinvention.

EXAMPLE 383

The process of Example 3, sample A, of U.S. Pat. No. 3,378,507 wasmodified to obtain a product having improved handling strength.

On an open two roll rubber mill, manufactured by the Bolling Company, 25parts of Novamont Corporation type F300 8N19 polypropylene and 75 partsof Ivory soap flakes were mixed for about ten minutes at a temperatureof about 350° F. until a homogeneous blend was formed. The material wasthen injection molded with a one-ounce Watson-Stillman injection moldingmachine having a mold cavity diameter of two inches and a depth of 20mils. The resulting sample was continuously washed for about three daysin a slowly flowing stream of tap water and then sequentially washed byimmersion in eight distilled water baths, each for a period of about onehour. The resulting sample still retained some soap. The resultingproduct was found to be stronger than the product of Example 382.

FIGS. 49 and 50 are photomicrographs of the product of Example 383 at195X and 2000X amplification, respectively. The irregular shapes shownby the photomicrographs are readily distinguishable from the structureof the present invention.

EXAMPLE 384

A porous polymer was prepared in accordance with Example II of U.S. Pat.No. 3,310,505, as modified to obtain a more homogeneous mixing of thematerials.

In a Brabender-Plasti-Corder internally heated blender, 40 parts ofExxon Chemical Corporation type LD 606 polyethylene and 60 parts of Rohmand Haas Corporation polymethylmethacrylate were mixed, for about 10minutes, at a machine temperature of about 350° F. until a homogeneousblend was formed. The material was then sheeted on a cold mill andsubsequently compression molded using a heated four-inch circular diewith a depth of 20 mils. and 30 tons of pressure for about ten minutes.The resulting composition was extracted for 48 hours with acetone in alarge Soxlet extractor.

FIGS. 53 and 54 are photomicrographs of the product of Example 384 at205X and 2000X amplification, respectively. The non-uniform structureshown by the photomicrographs is easily distinguished from the uniformstructure of the present invention.

PHYSICAL CHARACTERIZATION OF EXAMPLES 225 AND 358

To obtain a quantitative understanding of the homogeneous structure ofthe present invention, certain samples of the microporous material andcertain prior art samples were analyzed on an Aminco mercury intrusionporosimeter. FIGS. 30 and 31 are mercury intrusion curves of theone-half inch block of Example 225 which was made with 25 percentpolypropylene and 75 percent N,N-bis(2-hydroxyethyl)tallowamine, andFIG. 32 is a mercury intrusion curve of the 6 inch block of Example 225.All mercury intrusion curves are shown on a semi-log graph with theequivalent pore sizes shown on the log scale abscissa. FIGS. 30 through32 show the typical narrow distribution of pore sizes in the compositionof the instant invention. It was determined that the one-half inchsample of Example 225 has a void space of about 76 percent and anaverage pore size of about 0.5 micron and the 6 inch block has a voidspace of about 72 percent and an average pore size of about 0.6 micron.

FIG. 33 is a mercury intrusion curve of the product of Example 358 whichwas made with 40 percent polypropylene and 60 percentN,N-bis(2-hydroxyethyl)tallowamine. FIG. 33 shows that the sample hasthe typical narrow pore size distribution. It was determined that thesample had a void space of about 60 percent and an average pore size ofabout 0.15 micron.

It is readily apparent that the compositions of this invention have suchpore size distributions that at least 80 percent of the pore present inthe composition fall within no more than one decade on the abscissa ofthe mercury intrusion curve. The pore size distribution of thecomposition may thus be characterized as "narrow".

PHYSICAL CHARACTERIZATION OF PRIOR ART COMMERCIAL COMPOSITIONS EXAMPLE385

The composition of this example is commercially available Celgard 3501microporous polypropylene, manufactured by Celanese. FIG. 34 is amercury intrusion curve of the sample showing a large population ofpores in the range of 70 to 0.3 microns. The sample was determined tohave a void space of about 35 percent and an average pore size of about0.15 micron.

EXAMPLE 386

The composition of this example is commercially available A-20microporous polyvinylchloride, manufactured by Amerace. FIG. 35 is amercury intrusion curve of the sample and shows a very broad pore sizedistribution. The sample was determined to have a void space of about 75percent and an average pore size of about 0.16 microns.

EXAMPLE 387

The composition of this example is commercially available A-30microporous polyvinylchloride and manufactured by Amerace. FIG. 36 is amercury intrusion curve of the sample and shows a very wide pore sizedistribution. The sample was determined to have a void space of about 80percent and an average pore size of about 0.2 micron.

EXAMPLE 388

The composition of this example is commercially available Porexmicroporous polypropylene. FIG. 37 is a mercury intrusion curve of thesample showing a very broad distribution of extremely small cells aswell as a distribution of very large cells. The sample was determined tohave a void space of about 12 percent and an average pore size of aboutone micron.

EXAMPLE 389

The composition of this example is commercially available Millipore BDWP29300 microporous polyvinylchloride. FIG. 38 is a mercury intrusioncurve of the sample showing a relatively narrow distribution in therange of 0.5 to 2 microns as well as a number of cells smaller thanabout 0.5 micron. The sample was determined to have a void space ofabout 72 percent and an average pore size of about 1.5 microns.

EXAMPLES 392 TO 399

These examples illustrate the polymer/compatible liquid concentrationrange useful for the formation of homogeneous porous polymerintermediates from polymethylmethacylate and 1,4-butane diol using thestandard preparation procedure. In each example the intermediate formedwas about 0.5 inches in depth and about 2.5 inches in diameter. Thepolymethylmethacrylate was supplied by Rohm and Haas under thedesignation Plexiglas Acrylic Plastic Molding Powder, lot number 386491.The details of preparation are set forth in Table XXVII:

                  TABLE XXVII                                                     ______________________________________                                        EXAMPLE NO.    % LIQUID   TEMP., °C.                                   ______________________________________                                        392            90         215                                                 393            85         225                                                 394            80         225                                                 395            70         210                                                 396            60         229                                                 397            50         230                                                 398            40         229                                                 399            30         225                                                 ______________________________________                                    

The 1,4-butanediol was removed from the product of Example 395 and theresultant structure was determined to be the cellullar structure of thepresent invention, as may be seen from FIG. 61 which shows themicroporous product at 5000X amplification. The same polymer/liquidsystem as that of Example 394 was also cooled at rates up to 400° C. perminute and still produced the cellular structure of the presentinvention.

EXAMPLE 400

The porous polymer intermediate was prepared using the standardpreparation procedure and heating 30 percent polymethylmethacrylate, asutilized in the previous examples, and 70 percent lauric acid to 175° C.and cooling to form the porous polymer intermediate. The lauric acid wasremoved from the resultant intermediate to form the microporous cellularstructure of the present invention.

EXAMPLE 401

The porous polymer intermediate was prepared using the standardpreparation procedure and heating 30 percent Nylon 11, supplied byAldrich Chemical Company, and 70 percent ethylene carbonate to atemperature of 218° C. and then cooling the resultant solution to formthe porous polymer intermediate. The ethylene carbonate was removed fromthe intermediate and the resultant microporous polymer was determined tohave the cellular structure of the present invention.

EXAMPLE 402

The porous polymer intermediate was prepared using the standardpreparation procedure and heating 30 percent Nylon 11, as utilized inthe previous Example, and 70 percent 1,2-propylene carbonate was removedfrom the intermediate and the resultant microporous polymer wasdetermined to have the cellular structure of the present invention.

EXAMPLES 403-422

Examples 403-422 demonstrate the formation of the porous polymerintermediates from polymer/liquid systems containing various amounts ofNylon 11, as utilized in previous Examples, and tetramethylene sulfone,supplied by Shell under the designation Sulfone W, and containingapproximately 2.5 percent water. The various concentrations were cooledat various rates and from various solution temperatures, as indicated inTable XXVIII; which also demonstrates that increased cooling rates andincreased concentration of the polymer cause the resulting cell sizes todecrease, in general.

                  TABLE XXVIII                                                    ______________________________________                                                                  Cooling Rate                                                                           Cell Size                                  Ex. No. % Liq.  T °C.                                                                            °C./Min.                                                                        (Microns)                                  ______________________________________                                        403     90      195       20       10                                         404     80      198       5        15                                         405     80      198       20       14                                         406     80      198       40       9                                          407     80      198       80       5.5                                        408     70      200       5        11                                         409     70      200       20       5                                          410     70      200       40       6.5                                        411     70      200       80       6.5                                        412     60      205       5        5.                                         413     60      205       20       4.5                                        414     60      205       40       4                                          415     60      205       80       3.5                                        416     50      210       20       3                                          417     50      210       40       1.5                                        418     50      210       80       2                                          419     60      212       20       --                                         420     70      215       20       --                                         421     80      217       20       --                                         422     90      220       20       --                                         ______________________________________                                    

The foregoing Table XXVIII also demonstrates that at concentrations from40 percent to 10 percent liquid, there is no resulting visible porosity,for the system cooled at 20° C. per minute. Such results are entirelyanticipated as may be seen by referring to FIG. 62 which shows the meltcurve for the Nylon 11/tetramethylene Sulfone concentration range, aswell as the crystallization curves at the various rates of cooling. Itis apparent from FIG. 62 that at 20° C./minute cooling rate, the systemcontaining 40% liquid does not fall within the substantially flatportion of the crystallization curve and thus would not be expected toform the desired microporous structure. FIG. 63 is a photomicrograph at2000X amplification of Example 409 showing the typical cellularstructure of Examples 403-418.

EXAMPLE 423

The porous polymer intermediate was prepared by using the standardpreparation procedure and heating 30 percent polycarbonate supplied byGeneral Electric under the designation Lexan and 70 percent methanol toa temperature of 206° C. and cooling to form the porous polymerintermediate. The menthol was extracted and a cellular microporousstructure resulted as shown in FIG. 64, which is a photomicrograph ofthe product of this Example at 2000X amplification.

EXAMPLE 424

This Example demonstrates the formation of the microporous cellularstructure of the present invention from poly-2,6-dimethyl-1,4-phenyleneoxide, supplied by Scientific Polymer Products, commonly referred to aspolyphenylene oxide. The homogeneous microporous polymer intermediatewas made from 30 percent of said polyphenylene oxide and 70 percentN,N-bis(2-hydroxyethyl)tallowamine which was heated to a solutiontemperature of 275° C. and the intermediate was formed using thestandard preparation procedure. The liquid was removed from theintermediate and the cellular structure of the present inventionresulted, as may be seen from FIG. 65 which is a photomicrograph of theproduct of this Example at 2000X amplification.

EXAMPLE 425

This Example demonstrates the formation of the non-cellular product ofthis invention by cooling a homogeneous solution of 40 percentpolypropylene, as utilized in the previous Examples, and 60 percentdibutyl phthalate. The solution was extruded onto a chilled belt at athickness of about 10 mils and the cooling rate was in excess of 2,400°C./min. A quantity of dispersol was applied to the surface of the beltat a point prior to the solution being extruded thereon. The liquid wasremoved from the resultant film and a non-cellular microporous productresulted, as may be seen from FIG. 65 which is a photomicrograph of theproduct of this Example at 2000X amplification.

EXAMPLE 426

This Example demonstrates the formation of the non-cellular product ofthis invention by cooling a homogeneous solution of 25 percentpolypropylene, as utilized in previous examples, and 75 percentN,N-bis(2-hydroxyethyl)tallowamine in the same manner as that of Example425. The liquid was removed from the resultant film and a non-cellularmicroporous product resulted, as may be seen from FIG. 67 which is aphotomicrograph of the product of this Example at 2000X amplification.

The products of Examples 425 and 426 were analyzed by mercury intrusionporosimetry and their respective intrusion curves are shown in FIGS. 68and 69. It is apparent that both products have generally narrow poresize distributions, but the product of Example 426 demonstrates a muchnarrower distribution than the product of Example 425. Thus, the productof Example 425 has a calculated S value of 24.4 whereas the product ofExample 426 has a calculated S value of only 8.8. The average pore sizeof Example 425 is, however, very small, 0.096 microns, whereas theaverage pore size of the product of Example 426 is 0.589.

To quantitatively demonstrate the uniqueness of the cellularcompositions of the present invention, a number of such microporousproducts were prepared in accordance with the standard preparationprocedure and the details relating thereto are summarized in Examples427-457 in Table XXIX. The products of said Examples were analyzed bymercury intrusion porosity to determine their respective average porediameter and the S values and by scanning electron microscopy todetermine their average cell size, S. The result of such analysis areshown in Table XXX.

                  TABLE XXIX                                                      ______________________________________                                                                              Solution                                Ex.                              %    Temp.                                   No.  Polymer      Liquid         Void °C.                              ______________________________________                                        427  polypropylene                                                                              N,N--bis(2-hydroxyl-                                                                         75   180                                                       ethyl) tallowamine                                          428  polypropylene                                                                              N,N--bis(2-hydroxyl-                                                                         60   210                                                       ethyl) tallowamine                                          429  polypropylene                                                                              diphenylether  90   200                                     430  polypropylene                                                                              diphenylether  80   200                                     431  polypropylene                                                                              diphenylether  70   200                                     432  polypropylene                                                                              1,8-diaminooctane                                                                            70   180                                     433  polypropylene                                                                              phenylsalicylate                                                                             70   240                                     434  polypropylene                                                                              4-bromodiphenyl-                                                                             70   200                                                       ether                                                       435  polypropylene                                                                              tetrabromoethane                                                                             90   180                                     436  polypropylene                                                                              N--octyldiethanol-                                                                           75   --                                                        amine                                                       437  polypropylene                                                                              N--hexyldiethanol-                                                                           75   260                                                       amine                                                       438  polypropylene                                                                              salicylaldehyde                                                                              70   185                                     439  low density  hexanoic acid  70   190                                          polyethylene                                                             440  low density  l-octanol      70   178                                          polyethylene                                                             441  low density  dibutyl sebacate                                                                             70   238                                          polyethylene                                                             442  low density  Phosclere EC-53                                                                              70   191                                          polyethylene                                                             443  low density  dicapryl adipate                                                                             70   204                                          polyethylene                                                             444  low density  diisooctyl phthalate                                                                         70   204                                          polyethylene                                                             445  low density  dibutyl phthalate                                                                            70   290                                          polyethylene                                                             446  high density N,N--bis(2-hydroxyl-                                                                         80   250                                          polyethylene ethyl) tallowamine                                          447  polystyrene  l-dodecanol    75   220                                     448  polystyrene  1,3-bis(4-piperdine)                                                                         70   186                                                       propane                                                     449  polystyrene  diphenylamine  70   235                                     450  polystyrene  N--hexyldiethanol-                                                                           75   260                                                       amine                                                       451  polystyrene  Phosclere P315C                                                                              70   270                                     452  polymethylmeth-                                                                            1,4-butanediol 70   --                                           acrylate                                                                 453  polymethylmeth-                                                                            1,4-butanediol 85   --                                           acrylate                                                                 454  Surlyn       diphenylether  70   185-207                                 455  Surlyn       dibutyl phthalate                                                                            70   195                                     456  Noryl        N,N--bis(2-hydroxyl-                                                                         75   250                                                       ethyl) tallowamine                                          457  Nylon 11     ethylene carbonate                                                                           70   --                                      ______________________________________                                    

                  TABLE XXX                                                       ______________________________________                                        Ex. No.                                                                              C      P        C/P    S    log C/P                                                                              log S/C                             ______________________________________                                        427     5.0   0.520    9.6    2.86 0.982  -0.243                              428    3.18   0.112    28.4   5.0  1.45   0.197                               429    22.5   11.6     1.94   4.52 0.288  -0.697                              430    6.49   0.285    22.8   27.1 1.36   0.621                               431    6.72   0.136    49.4   7.01 1.69   0.0183                              432    13.0   0.498    26.1   2.36 1.42   -0.741                              433    13.8   0.272    50.7   4.29 1.71   -0.507                              434    3.35   0.137    24.5   5.25 1.39   0.195                               435    15.4   0.804    19.2   5.13 1.28   -0.477                              436    16.6   0.850    19.5   2.52 1.29   -0.819                              437    20.0   0.631    31.7   2.51 1.50   -0.901                              438    7.9    0.105    75.2   3.22 1.88   -0.390                              439    7.5    1.16     6.47   8.62 0.811  0.0604                              440    6.8    1.00     6.8    3.53 0.833  0.285                               441    5.85   0.636    9.20   6.07 0.964  0.0160                              442    3.40   0.512    6.64   5.30 0.822  0.193                               443    5.0    0.871    5.74   8.21 0.759  0.215                               444    4.75   0.631    7.53   3.54 0.877  -0.128                              445    7.8    1.18     6.61   3.82 0.820  -0.310                              446    34.5   0.696    49.6   4.34 1.70   -0.900                              447    28.2   1.88     15.0   3.40 1.18   -0.919                              448    1.08   0.0737   14.7   2.87 1.17   0.424                               449    6.65   0.631    10.5   63.5 1.02   0.980                               450    7.4    0.164    45.1   3.74 1.65   -0.296                              451    1.4    0.151    9.27   2.26 0.967  0.208                               452    9.2    0.201    45.8   3.68 1.66   -0.398                              453    114    10.3     11.1   5.19 1.05   -1.34                               454    6.8    0.631    10.8   2.13 1.03   -0.504                              455    5.6    0.769    7.28   2.09 0.862  -0.428                              456    19.0   0.179    106    2.74 2.03   -0.841                              457    5.8    0.372    15.6   7.56 1.19   0.112                               ______________________________________                                    

                  TABLE XXXI                                                      ______________________________________                                        Ex. No.   Prior Art Description                                                                          Polymer Type                                       ______________________________________                                        458       Celgard 3501     polypropylene                                      459       Amerace A-30     polyvinylchloride                                  460       Porex            polypropylene                                      461       Milipore EG      cellulosic                                         462       Metricel GA-8    cellulosic                                         463       Sartorius SM 12807                                                                             polyvinylchloride                                  464       Millipore HAWP   cellulosic                                         465       Millipore G5WP 04700                                                                           cellulosic                                         466       Millipore VMWP 04700                                                                           cellulosic                                         467       Amicon 5UMO5     cellulosic                                         468       Celgard 2400     polypropylene                                      469       Millipore SMWP 04700                                                                           polyvinylchloride                                  470       Celgard 2400     polypropylene                                      471       Product of Example 381                                                                         polyethylene                                       472       Product of Example 380                                                                         polyethylene                                       473       Product of Example 383                                                                         polypropylene                                      474       Product of Example 384                                                                         polyethylene                                       ______________________________________                                    

                  TABLE XXXII                                                     ______________________________________                                        Ex. No.  C             S       log S/C                                        ______________________________________                                        458      0.04*         2.32    1.76                                           459      0.3           138     2.66                                           460      186           2.41    -1.89                                          461      0.2*          26.3    1.85                                           462      0.2*          9.14    1.66                                           463      0.2*          31.5    2.2                                            464      0.8*          2.94    0.565                                          465      0.22*         1.64    0.872                                          466      0.05*         5.37    2.03                                           467      2.10**        61.8    1.79                                           468      0.02*         5.08    2.40                                           469      5*            1.55    -0.509                                         470      0.04*         5.64    2.15                                           471      1.1**         11.5    1.019                                          472      0.8**         17.5    1.34                                           473      0.56          16.8    1.477                                          474      70            1.34    -1.718                                         ______________________________________                                         *From company product information                                             **From mercury intrusion                                                 

The data contained in Tables XXIX through XXXII is summarized in FIG. 70which is a plot of the log S/C vs. log C/P. From FIG. 70 it is apparentthat the cellular structure of the present invention may be defined ashaving a log C/P of from about 0.2 to about 2.4 and a log S/C of fromabout -1.4 to about 1.0, and more usually said polymer will have a logC/P of from about 0.6 to about 2.2 and a log S/C of from about -0.6 toabout 0.4.

Thus, as has been seen, the present invention provides a facile methodfor preparing microporous polymers from any synthetic thermoplasticpolymer in widely varying thicknesses and shapes. The microporouspolymers may possess a unique microcellular configuration and are in anyevent characterized by pore diameters with relatively narrow sizedistribution. These structures are formed by first selecting a liquidthat is compatible with a polymer, i.e.--forms a homogeneous solutionwith the polymer and can be removed from the polymer after cooling andthen selecting the amount of the liquid and carrying out the cooling ofthe solution in a fashion which insures that the desired microporouspolymer configuration will result.

As can be also seen, the present invention also provides microporouspolymer products which contain relatively large amounts of functionallyuseful liquids such as a polymer additive and behave as a solid. Theseproducts may be advantageously utilized in a variety of applicationssuch as, for example, in masterbatching.

What is claimed is:
 1. A relatively homogeneous, three-dimensional,microporous cellular polymer structure comprising a plurality ofsubstantially spherical cells having an average diameter from about 0.5to about 100 microns, distributed substantially uniformly throughout thestructure, adjacent cells being interconnected by pores smaller indiameter than said microcells, the ratio of the average cell diameter tothe average pore diameter being from about 2:1 to about 200:1, saidpores and said cells being void and said polymer being a syntheticthermoplastic polymer selected from the group consisting of olefinicpolymers, condensation polymers, oxidation polymers and blends thereof.2. The polymer structure of claim 1 wherein said polymer is an olefinicpolymer.
 3. The polymer structure of claim 2 wherein the ratio of theaverage cell diameter to the average pore diameter is from about 5:1 toabout 40:1.
 4. The polymer structure of claim 3 wherein the average celldiameter is from about 1 to about 20 microns and the average porediameter is from about 0.05 to about 10 microns.
 5. The polymerstructure of claim 4 wherein the average pore size is from about 0.1 toabout 1.0 micron.
 6. The polymer structure of claim 5 wherein thepolymer is a non-acrylic polyoefin.
 7. The polymer structure of claim 6wherein the polymer is selected from the group consisting of low densitypolyethylene, high density polyethylene, polypropylene, polystyrene,polyvinylchloride, acrylonitrile-butadiene-styrene terpolymers,styrene-acrylonitrile copolymers, styrene butadiene copolymers,poly(4-methyl-pentene-1), polybutylene, polyvinylidene chloride,polyvinyl butyral, chlorinated polyethylene, ethylene-vinyl acetatecopolymers, polyvinyl acetate and polyvinyl alcohol.
 8. The polymerstructure of claim 5 wherein the polymer is an acrylic polyolefin. 9.The polymer structure of claim 8 wherein the polymer is selected fromthe group consisting of polymethyl-methacrylate, polymethyl-acrylate,ethylene-acrylic acid copolymers, and ethylene-acrylic acid metal saltcopolymers.
 10. The polymer structure of claim 1 wherein the polymer isan oxidation polymer.
 11. The polymer structure of claim 10 wherein theratio of the average cell diameter to the average pore diameter is fromabout 5:1 to about 40:1.
 12. The polymer structure of claim 11 whereinthe average cell diameter is from about 1 to about 20 microns and theaverage pore diameter is from about 0.05 to about 10 microns.
 13. Thepolymer structure of claim 12 wherein the average pore diameter is fromabout 0.1 to about 1.0 micron.
 14. The polymer structure of claim 13wherein the polymer is polyphenylene oxide.
 15. The polymer structure ofclaim 1 wherein said polymer is a condensation polymer.
 16. The polymerstructure of claim 15 wherein the ratio of the average cell diameter tothe average pore diameter is from about 5:1 to about 40:1.
 17. Thepolymer structure of claim 16 wherein the average cell diameter is fromabout 1 to about 20 microns and the average pore diameter is from about0.05 to about 10 microns.
 18. The polymer structure of claim 17 whereinthe average pore diameter is from about 0.1 to about 1.0 microns. 19.The polymer structure of claim 18 wherein the polymer is selected fromthe group consisting of polyethylene terephthalate, polybutyleneterephthalate, Nylon 6, Nylon 11, Nylon 13, Nylon 66, polycarbonates andpolysulfone.
 20. The polymer structure of claim 1 wherein the polymer isa non-acrylic polyolefin.
 21. The polymer structure of claim 1 whereinthe polymer is selected from the group consisting of low densitypolyethylene, high density polyethylene, polypropylene, polystyrene,polyvinylchloride, acrylonitrile-butadiene-styrene terpolymers,styrene-acrylonitrile copolymers, styrene butadiene copolymers,poly(4-methyl-pentene-1), polybutylene, polyvinylidene chloride,polyvinyl butyral, chlorinated polyethylene, ethylene-vinyl acetatecopolymers, polyvinyl acetate and polyvinyl alcohol.
 22. The polymerstructure of claim 1 wherein the polymer is an acrylic polyolefin. 23.The polymer structure of claim 1 wherein the polymer is selected fromthe group consisting of polymethyl-methacrylate, polymethyl-acrylate,ethylene-acrylic acid copolymers, and ethylene-acrylic acid metal saltcopolymers.
 24. The polymer structure of claim 1 wherein the polymer ispolyphenylene oxide.
 25. The polymer structure of claim 1 wherein thepolymer is selected from the group consisting of polyethyleneterephthalate, polybutylene terephthalate, Nylon 6, Nylon 11, Nylon 13,Nylon 66, polycarbonates and polysulfone.
 26. The polymer structures ofclaim 1 wherein said structure is in the form of a block having athickness up to about 21/2 inches.
 27. The polymer structure of claim 1wherein said structure has an essentially non-cellular skin.
 28. Thepolymer structure of claim 27 wherein said skin is relatively imperviousto the passage of liquid.
 29. The polymer structure of claim 1 whereinsaid structure is in the form of a film.
 30. A microporous cellularpolymer structure comprising a synthetic thermoplastic polymer selectedfrom the group consisting of olefinic polymers, condensation polymers,oxidation polymers, and blends thereof characterized by a C/P ratio offrom about 2 to about 200, an S value of from about 1 to about 30, andan average cell size from about 0.5 to about 100 microns.
 31. Thepolymer structure of claim 30 wherein the polymer is selected from thegroup consisting of low density polyethylene, high density polyethylene,polypropylene, polystyrene, polyvinylchloride,acrylonitrile-butadiene-styrene terpolymers, styrene-acrylonitrilecopolymers, styrene-butadiene copolymers, poly(4-methyl-pentene-1),polybutylene, polyvinylidene chloride, polyvinyl butyral, chlorinatedpolyethylene, ethylene-vinyl acetate copolymers, polyvinyl acetate andpolyvinyl alcohol.
 32. The polymer structure of claim 30 wherein thepolymer is selected from the group consisting ofpolymethyl-methacrylate, polymethyl-acrylate, ethylene-acrylic acidcopolymers, and ethylene-acrylic acid metal salt copolymers.
 33. Thepolymer of claim 30 wherein the polymer is polyphenylene oxide.
 34. Thepolymer structure of claim 30 wherein the polymer is selected from thegroup consisting of polyethylene terephthalate, polybutyleneterephthalate, Nylon 6, Nylon 11, Nylon 13, Nylon 66, polycarbonates andpolysulfone.
 35. The polymer structure of claim 30 wherein the C/P ratiois from about 5 to about 40, the S value is from about 2 to about 10,and the average cell size is from about 1 to about 20 microns.
 36. Amicroporous cellular structure comprising a synthetic thermoplasticpolymer selected from the group consisting of olefinic polymers,condensation polymers, oxidation polymers and blends thereofcharacterized by a log C/P value of from about 0.2 to about 2.4 and alog S/C value of from about -1.4 to about 1.0.
 37. The polymer structureof claim 36 wherein the polymer is selected from the group consisting oflow density polyethylene, polypropylene, polystyrene, polyvinylchloride,acrylonitrile-butadiene-styrene terpolymers, styrene-acrylonitrilecopolymers, styrene butadiene copolymers, poly(4-methyl-pentene-1),polybutylene, polyvinylidene chloride, polyvinyl butyral, chlorinatedpolyethylene, ethylene-vinyl acetate copolymers, polyvinyl acetate andpolyvinyl alcohol.
 38. The polymer structure of claim 36 wherein thepolymer is selected from the group consisting ofpolymethyl-methacrylate, polymethyl-acrylate, ethylene-acrylic acidcopolymers and ethylene-acrylic acid metal salt copolymers.
 39. Thepolymer structure of claim 36 wherein the polymer is polyphenyleneoxide.
 40. The polymer structure of claim 36 wherein the polymer isselected from the group consisting of polyethylene terephthalate,polybutylene terephthalate, Nylon 6, Nylon 11, Nylon 13, Nylon 66,polycarbonates and polysulfone.
 41. The polymer structure of claim 36wherein the log C/P value is from about 0.6 to about 2.2 and the log S/Cvalue is from about -0.6 to about 0.4.
 42. An isotropic microporouspolymer structure comprising a synthetic thermoplastic polymer selectedfrom the group consisting of olefinic polymers, oxidation polymers, andblends thereof characterized by an average pore diameter of from about0.1 to about 5 microns and an S value of from about 1 to about
 10. 43.The polymer structure of claim 42 wherein the polymer is selected fromthe group consisting of low density polyethylene, high densitypolyethylene, polypropylene, polystyrene, polyvinylchloride,acrylonitrile-butadiene-styrene terpolymers, styrene-acrylonitrilecopolymers, styrene butadiene copolymers, poly(4-methyl-pentene-1),polybutylene, polyvinylidene chloride polyvinyl butyral, chlorinatedpolyethylene, ethylenevinyl acetate copolymers, polyvinyl acetate andpolyvinyl alcohol.
 44. The polymer structure of claim 42 wherein thepolymer is selected from the group consisting ofpolymethyl-methacrylate, polymethyl-acrylate, ethylene-acrylic acidcopolymers, and ethylene-acrylic acid metal salt copolymers.
 45. Thepolymer structure of claim 42 wherein the polymer is polyphenyleneoxide.
 46. The polymer structure of claim 42 wherein the average porediameter is from about 0.2 to about 1 micron and the S value is fromabout 5 to about
 10. 47. A relatively homogeneous, three-dimensional,microporous cellular polymer structure comprising a plurality ofsubstantially spherical cells having an average diameter from about 0.5to about 100 microns, distributed substantially uniformly throughout thestructure, adjacent cells being interconnected by pores smaller indiameter than said microcells, the ratio of the average cell diameter tothe average pore diameter being from about 2:1 to about 200:1, saidpolymer being a synthetic thermoplastic polymer selected from the groupconsisting of olefinic polymers, condensation polymers, oxipolymers andblends thereof, and said cells and pores being at least partially filledwith a liquid lubricant.
 48. A relatively homogeneous,three-dimensional, microporous cellular polymer structure comprising aplurality of substantially spherical cells having an average diameterfrom about 0.5 to about 100 microns, distributed substantially uniformlythroughout the structure, adjacent cells being interconnected by poressmaller in diameter than said microcells, the ratio of the average celldiameter to the average pore diameter being from about 2:1 to about200:1, said polymer being a synthetic thermoplastic polymer selectedfrom the group consisting of olefinic polymers, condensation polymers,oxipolymers and blends thereof, and said cells and pores being at leastpartially filled with a liquid surfactant.
 49. A relatively homogeneous,three-dimensional, microporous cellular polymer structure comprising aplurality of substantially spherical cells having an average diameterfrom about 0.5 to about 100 microns, distributed substantially uniformlythroughout the structure, adjacent cells being interconnected by poressmaller in diameter than said microcells, the ratio of the average celldiameter to the average pore diameter being from about 2:1 to about200:1, said polymer being a synthetic thermoplastic polymer selectedfrom the group consisting of olefinic polymers, condensation polymers,oxipolymers and blends thereof, and said cells and pores being at leastpartially filled with a liquid slip agent.
 50. A relatively homogeneous,three-dimensional, microporous cellular polymer structure comprising aplurality of substantially spherical cells having an average diameterfrom about 0.5 to about 100 microns, distributed substantially uniformlythroughout the structure, adjacent cells being interconnected by poressmaller in diameter than said microcells, the ratio of the average celldiameter to the average pore diameter being from about 2:1 to about200:1, said polymer being a synthetic thermoplastic polymer selectedfrom the group consisting of olefinic polymers, condensation polymers,oxipolymers and blends thereof, and said cells and pores being at leastpartially filled with a liquid moth repellant.
 51. A relativelyhomogeneous, three-dimensional, microporous cellular polymer structurecomprising a plurality of substantially spherical cells having anaverage diameter from about 0.5 to about 100 microns, distributedsubstantially uniformly throughout the structure, adjacent cells beinginterconnected by pores smaller in diameter than said microcells, theratio of the average cell diameter to the average pore diameter beingfrom about 2:1 to about 200:1, said polymer being a syntheticthermoplastic polymer selected from the group consisting of olefinicpolymers, condensation polymers, oxipolymers and blends thereof, andsaid cells and pores being at least partially filled with a liquidpesticide.
 52. A relatively homogeneous, three-dimensional, microporouscellular polymer structure comprising a plurality of substantiallyspherical cells having an average diameter from about 0.5 to about 100microns, distributed substantially uniformly throughout the structure,adjacent cells being interconnected by pores smaller in diameter thansaid microcells, the ratio of the average cell diameter to the averagepore diameter being from about 2:1 to about 200:1, said polymer being asynthetic thermoplastic polymer selected from the group consisting ofolefinic polymers, condensation polymers, oxipolymers and blendsthereof, and said cells and pores being at least partially filled with aliquid plasticizer.
 53. A relatively homogeneous, three-dimensional,microporous cellular polymer structure comprising a plurality ofsubstantially spherical cells having an average diameter from about 0.5to about 100 microns, distributed substantially uniformly throughout thestructure, adjacent cells being interconnected by pores smaller indiameter than said microcells, the ratio of the average cell diameter tothe average pore diameter being from about 2:1 to about 200:1, saidpolymer being a synthetic thermoplastic polymer selected from the groupconsisting of olefinic polymers, condensation polymers, oxipolymers andblends thereof, and said cells and pores being at least partially filledwith a liquid medicinal.
 54. A relatively homogeneous,three-dimensional, microporous cellular polymer structure comprising aplurality of substantially spherical cells having an average diameterfrom about 0.5 to about 100 microns, distributed substantially uniformlythroughout the structure, adjacent cells being interconnected by poressmaller in diameter than said microcells, the ratio of the average celldiameter to the average pore diameter being from about 2:1 to about200:1, said polymer being a synthetic thermoplastic polymer selectedfrom the group consisting of olefinic polymers, condensation polymers,oxipolymers and blends thereof, and said cells and pores being at leastpartially filled with a liquid fuel additive.
 55. A relativelyhomogeneous, three-dimensional, microporous cellular polymer structurecomprising a plurality of substantially spherical cells having anaverage diameter from about 0.5 to about 100 microns, distributedsubstantially uniformly throughout the structure, adjacent cells beinginterconnected by pores smaller in diameter than said microcells, theratio of the average cell diameter to the average pore diameter beingfrom about 2:1 to about 200:1, said polymer being a syntheticthermoplastic polymer selected from the group consisting of olefinicpolymers, condensation polymers, oxipolymers and blends thereof, andsaid cells and pores being at least partially filled with a liquidpolishing agent.
 56. A relatively homogeneous, three-dimensional,microporous cellular polymer structure comprising a plurality ofsubstantially spherical cells having an average diameter from about 0.5to about 100 microns, distributed substantially uniformly throughout thestructure, adjacent cells being interconnected by pores smaller indiameter than said microcells, the ratio of the average cell diameter tothe average pore diameter being from about 2:1 to about 200:1, saidpolymer being a synthetic thermoplastic polymer selected from the groupconsisting of olefinic polymers, condensation polymers, oxipolymers andblends thereof, and said cells and pores being at least partially filledwith a liquid insect repellant.
 57. A relatively homogeneous,three-dimensional, microporous cellular polymer structure comprising aplurality of substantially spherical cells having an average diameterfrom about 0.5 to about 100 microns, distributed substantially uniformlythroughout the structure, adjacent cells being interconnected by poressmaller in diameter than said microcells, the ratio of the average celldiameter to the average pore diameter being from about 2:1 to about200:1, said polymer being a synthetic thermoplastic polymer selectedfrom the group consisting of olefinic polymers, condensation polymers,oxipolymers and blends thereof, and said cells and pores being at leastpartially filled with a liquid animal repellant.
 58. A relativelyhomogeneous, three-dimensional, microporous cellular polymer structurecomprising a plurality of substantially spherical cells having anaverage diameter from about 0.5 to about 100 microns, distributedsubstantially uniformly throughout the structure, adjacent cells beinginterconnected by pores smaller in diameter than said microcells, theratio of the average cell diameter to the average pore diameter beingfrom about 2:1 to about 200:1, said polymer being a syntheticthermoplastic polymer selected from the group consisting of olefinicpolymers, condensation polymers, oxipolymers and blends thereof, andsaid cells and pores being at least partially filled with a liquidfragrance.
 59. A relatively homogeneous, three-dimensional, microporouscellular polymer structure comprising a plurality of substantiallyspherical cells having an average diameter from about 0.5 to about 100microns, distributed substantially uniformly throughout the structure,adjacent cells being interconnected by pores smaller in diameter thansaid microcells, the ratio of the average cell diameter to the averagepore diameter being from about 2:1 to about 200:1, said polymer being asynthetic thermoplastic polymer selected from the group consisting ofolefinic polymers, condensation polymers, oxipolymers and blendsthereof, and said cells and pores being at least partially filled with aliquid flame retardant.
 60. A relatively homogeneous, three-dimensional,microporous cellular polymer structure comprising a plurality ofsubstantially spherical cells having an average diameter from about 0.5to about 100 microns, distributed substantially uniformly throughout thestructure, adjacent cells being interconnected by pores smaller indiameter than said microcells, the ratio of the average cell diameter tothe average pore diameter being from about 2:1 to about 200:1, saidpolymer being a synthetic thermoplastic polymer selected from the groupconsisting of olefinic polymers, condensation polymers, oxipolymers andblends thereof, and said cells and pores being at least partially filledwith a liquid antioxidant.
 61. A relatively homogeneous,three-dimensional, microporous cellular polymer structure comprising aplurality of substantially spherical cells having an average diameterfrom about 0.5 to about 100 microns, distributed substantially uniformlythroughout the structure, adjacent cells being interconnected by poressmaller in diameter than said microcells, the ratio of the average celldiameter to the average pore diameter being from about 2:1 to about200:1, said polymer being a synthetic thermoplastic polymer selectedfrom the group consisting of olefinic polymers, condensation polymers,oxipolymers and blends thereof, and said cells and pores being at leastpartially filled with a liquid odor masking agent.
 62. A relativelyhomogeneous, three-dimensional, microporous cellular polymer structurecomprising a plurality of substantially spherical cells having anaverage diameter from about 0.5 to about 100 microns, distributedsubstantially uniformly throughout the structure, adjacent cells beinginterconnected by pores smaller in diameter than said microcells, theratio of the average cell diameter to the average pore diameter beingfrom about 2:1 to about 200:1, said polymer being a syntheticthermoplastic polymer selected from the group consisting of olefinicpolymers, condensation polymers, oxipolymers and blends thereof, andsaid cells and pores being at least partially filled with a liquidantifogging agent.
 63. A relatively homogeneous, three-dimensional,microporous cellular polymer structure comprising a plurality ofsubstantially spherical cells having an average diameter from about 0.5to about 100 microns, distributed substantially uniformly throughout thestructure, adjacent cells being interconnected by pores smaller indiameter than said microcells, the ratio of the average cell diameter tothe average pore diameter being from about 2:1 to about 200:1, saidpolymer being a synthetic thermoplastic polymer selected from the groupconsisting of olefinic polymers, condensation polymers, oxipolymers andblends thereof, and said cells and pores being at least partially filledwith a liquid perfume.